LITHIUM-SULFUR BATTERIES

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26220%2F15%3APU114135" target="_blank" >RIV/00216305:26220/15:PU114135 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
čeština
Název v původním jazyce
LITHIUM-SULFUR BATTERIES
Popis výsledku v původním jazyce
In this paper I present fundamental characteristics, principle, measurement and preparation cathode materials of Li-S batteries. S+C (sulfur+carbon) cathode material was prepared by simple solid-state reaction in ball mill. Content of sulphur was approximately 80 wt. % in final sample. Cyclic voltammetry and galvanostatic charge/discharge techniques were used for characterization of the samples. Initial discharge capacity observed for S+C sample was 600 mAh/gsulfur. Capacity loss for S+C sample after 30th cycles was 66 %. Cycling loss is due to insoluble polysulfide formation.
Název v anglickém jazyce
LITHIUM-SULFUR BATTERIES
Popis výsledku anglicky
In this paper I present fundamental characteristics, principle, measurement and preparation cathode materials of Li-S batteries. S+C (sulfur+carbon) cathode material was prepared by simple solid-state reaction in ball mill. Content of sulphur was approximately 80 wt. % in final sample. Cyclic voltammetry and galvanostatic charge/discharge techniques were used for characterization of the samples. Initial discharge capacity observed for S+C sample was 600 mAh/gsulfur. Capacity loss for S+C sample after 30th cycles was 66 %. Cycling loss is due to insoluble polysulfide formation.

Projekt
<a href="/cs/project/LO1210" target="_blank" >LO1210: Energie v podmínkách udržitelného rozvoje (EN-PUR)</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>S - Specificky vyzkum na vysokych skolach

Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)