Elimination of Irreversible Effects During the First Charging of the Lithium Battery Anodes

Kód výsledku v IS VaVaI

RIV/00216305:26220/17:PU120835 - isvavai.cz

Výsledek na webu

http://eom.phys.asm.md/en/disclaimer

DOI - Digital Object Identifier

10.3103/S1068375517060059

Jazyk výsledku

angličtina

Název v původním jazyce

Elimination of Irreversible Effects During the First Charging of the Lithium Battery Anodes

Popis výsledku v původním jazyce

The irreversible capacity of negative electrode in a lithium-ion cell is a widely described the phenomenon. Irreversible capacity losses are connected with formation of a solid electrolyte interface layer. This layer is growing on the electrode-electrolyte interface during first several charging cycles. The layer is indispensable for proper functioning of a lithium-ion cell. However, during this layer formation, the atoms of lithium are consumed in a range from 18 to 45% of the total amount of lithium atoms presented in cell. Demonstration of possibilities to suppress this phenomenon that occurs on a negative electrode interface is the main aim of this paper.

Název v anglickém jazyce

Elimination of Irreversible Effects During the First Charging of the Lithium Battery Anodes

Popis výsledku anglicky

The irreversible capacity of negative electrode in a lithium-ion cell is a widely described the phenomenon. Irreversible capacity losses are connected with formation of a solid electrolyte interface layer. This layer is growing on the electrode-electrolyte interface during first several charging cycles. The layer is indispensable for proper functioning of a lithium-ion cell. However, during this layer formation, the atoms of lithium are consumed in a range from 18 to 45% of the total amount of lithium atoms presented in cell. Demonstration of possibilities to suppress this phenomenon that occurs on a negative electrode interface is the main aim of this paper.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10405 - Electrochemistry (dry cells, batteries, fuel cells, corrosion metals, electrolysis)

Projekt

LO1210: Energie v podmínkách udržitelného rozvoje (EN-PUR)

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

SURF ENG APPL ELECT+

ISSN

1068-3755

e-ISSN

1934-8002

Svazek periodika

6

Číslo periodika v rámci svazku

53

Stát vydavatele periodika

MD - Moldavská republika

Počet stran výsledku

9

Strana od-do

597-605

Kód UT WoS článku

000418600200012

EID výsledku v databázi Scopus

2-s2.0-85039039167