Study of the changes on the electrode structure at high temperature load by scanning electron microscope
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26220%2F17%3APU125006" target="_blank" >RIV/00216305:26220/17:PU125006 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1149/08101.0337ecst" target="_blank" >http://dx.doi.org/10.1149/08101.0337ecst</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1149/08101.0337ecst" target="_blank" >10.1149/08101.0337ecst</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Study of the changes on the electrode structure at high temperature load by scanning electron microscope
Popis výsledku v původním jazyce
One of biggest issues in current Li-Ion accumulators is thermal stability. Some of the active materials are more stable than other but usually materials with high capacity suffer by lower thermal stability. During heating there is not only decomposition of the cathode material but also other parts of the battery such as anode material, binders and electrolytes. From for that reason was tested entire electrode composition contain the cathode material, including the binder and conductive carbon deposited on the aluminum current collector. It was studied structural changes ongoing up to 400°C by scanning electron microscope and changes of elements composition in the electrode by electron dispersion analysis.
Název v anglickém jazyce
Study of the changes on the electrode structure at high temperature load by scanning electron microscope
Popis výsledku anglicky
One of biggest issues in current Li-Ion accumulators is thermal stability. Some of the active materials are more stable than other but usually materials with high capacity suffer by lower thermal stability. During heating there is not only decomposition of the cathode material but also other parts of the battery such as anode material, binders and electrolytes. From for that reason was tested entire electrode composition contain the cathode material, including the binder and conductive carbon deposited on the aluminum current collector. It was studied structural changes ongoing up to 400°C by scanning electron microscope and changes of elements composition in the electrode by electron dispersion analysis.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
10405 - Electrochemistry (dry cells, batteries, fuel cells, corrosion metals, electrolysis)
Návaznosti výsledku
Projekt
<a href="/cs/project/LO1210" target="_blank" >LO1210: Energie v podmínkách udržitelného rozvoje (EN-PUR)</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
ECS Transactions
ISBN
9788021451094
ISSN
1938-5862
e-ISSN
1938-6737
Počet stran výsledku
6
Strana od-do
337-341
Název nakladatele
Neuveden
Místo vydání
Neuveden
Místo konání akce
Antonínská 1, Brno
Datum konání akce
28. 8. 2016
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—