An In Vitro Corrosion Study of Open Cell Iron Structures with PEG Coating for Bone Replacement Applications

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26220%2F18%3APU128704" target="_blank" >RIV/00216305:26220/18:PU128704 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.mdpi.com/2075-4701/8/7/499" target="_blank" >http://www.mdpi.com/2075-4701/8/7/499</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.3390/met8070499" target="_blank" >10.3390/met8070499</a>

Jazyk výsledku

angličtina

Název v původním jazyce

An In Vitro Corrosion Study of Open Cell Iron Structures with PEG Coating for Bone Replacement Applications

Popis výsledku v původním jazyce

Iron-based substrates with polyethylene glycol coating were prepared as possible materials for biodegradable orthopedic implants. Biodegradable materials that provide mechanical support of the diseased tissue at the time of implanting and then disappear gradually during the healing process are sometimes favored instead of permanent implants. The implant degradation rate should match the time of the tissue regrowth. In this work, the degradation behavior of iron-based foams was studied electrochemically during immersion tests in Hanks’ solution. The corrosion rate of the polyethylene glycol-coated samples increased and the corrosion potential shifted to more negative values. This indicates an enhanced degradation rate as compared to the uncoated material, fulfilling the goal of being able to tune the degradation rate. It is the interfacial interaction between the hydrophilic polymer layer and the iron surface that is responsible for the enhanced oxidation rate of iron.

Název v anglickém jazyce

An In Vitro Corrosion Study of Open Cell Iron Structures with PEG Coating for Bone Replacement Applications

Popis výsledku anglicky

Iron-based substrates with polyethylene glycol coating were prepared as possible materials for biodegradable orthopedic implants. Biodegradable materials that provide mechanical support of the diseased tissue at the time of implanting and then disappear gradually during the healing process are sometimes favored instead of permanent implants. The implant degradation rate should match the time of the tissue regrowth. In this work, the degradation behavior of iron-based foams was studied electrochemically during immersion tests in Hanks’ solution. The corrosion rate of the polyethylene glycol-coated samples increased and the corrosion potential shifted to more negative values. This indicates an enhanced degradation rate as compared to the uncoated material, fulfilling the goal of being able to tune the degradation rate. It is the interfacial interaction between the hydrophilic polymer layer and the iron surface that is responsible for the enhanced oxidation rate of iron.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10405 - Electrochemistry (dry cells, batteries, fuel cells, corrosion metals, electrolysis)

Projekt

<a href="/cs/project/LO1210" target="_blank" >LO1210: Energie v podmínkách udržitelného rozvoje (EN-PUR)</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2018

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Metals

ISSN

2075-4701

e-ISSN

—

Svazek periodika

8

Číslo periodika v rámci svazku

7

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

21

Strana od-do

1-21

Kód UT WoS článku

000445096800029

EID výsledku v databázi Scopus

2-s2.0-85049196196