SOURCES OF DEGRADATION IN LI-S CELLS

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26220%2F18%3APU129365" target="_blank" >RIV/00216305:26220/18:PU129365 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

SOURCES OF DEGRADATION IN LI-S CELLS

Popis výsledku v původním jazyce

Lithium-sulfur batteries have attracted the focus of scientists for more than four decades [1-4]. This type of battery represents a promising system of high theoretical capacity, energy density, low cost and the non-toxicity of sulfur. Yet many challenges facing the Li-S technology exist, either with the materials or with the systems, such as a low utilization of sulfur, poor cycle life, high self-discharge rates and capacity fading [1], [3-5]. The degradation mechanisms in Li-S batteries, that are responsible for low sulfur utilization and capacity fading, are still unclear [3,6,7], since some mechanisms may lead to reversible or irreversible degradation [6]. Dominant sources of degradation are determined through Coulombic efficiency and energy efficiency dependences on the number of cycles and from the temperature evolution within the cell cycling.

Název v anglickém jazyce

SOURCES OF DEGRADATION IN LI-S CELLS

Popis výsledku anglicky

Lithium-sulfur batteries have attracted the focus of scientists for more than four decades [1-4]. This type of battery represents a promising system of high theoretical capacity, energy density, low cost and the non-toxicity of sulfur. Yet many challenges facing the Li-S technology exist, either with the materials or with the systems, such as a low utilization of sulfur, poor cycle life, high self-discharge rates and capacity fading [1], [3-5]. The degradation mechanisms in Li-S batteries, that are responsible for low sulfur utilization and capacity fading, are still unclear [3,6,7], since some mechanisms may lead to reversible or irreversible degradation [6]. Dominant sources of degradation are determined through Coulombic efficiency and energy efficiency dependences on the number of cycles and from the temperature evolution within the cell cycling.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20201 - Electrical and electronic engineering

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2018

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

39. Nekonvenční zdroje elektrické energie

ISBN

978-80-02-02786-7

ISSN

—

e-ISSN

—

Počet stran výsledku

3

Strana od-do

95-97

Název nakladatele

Neuveden

Místo vydání

Neuveden

Místo konání akce

Hustopeče

Datum konání akce

9. 5. 2018

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—