ULTRA-HIGH STRENGTH REACTIVE POWDER CONCRETES (MORTARS)

Popis výsledku v původním jazyce

The ultra-high strength of reactive powder concrete (RPC) is achieved due to the following factors very fine aggregate within 0 - 4 mm in size (preferably fused bauxite), proper kind and amount of superplasticizer and steel microfibers and substitution of a part of fine sand by steel powder. The possibility to ensure at least first period of setting under certain pressure is very effective. After 1 day of moist curing at ambient temperature, the compressive strengths exceed 80 MPa. After 28 days they even rise to 220 MPa. Thermal treatment at 250 and 400 causes the formation of crystalline xonotlite and the increase of compressive strengths above 350 MPa, reportedly even above 700 MPa. The study of the further chemical and physico-mechanical propertiesof these very promising high-strength and corrosion resistance performance composites has been in progress.

Název v anglickém jazyce

ULTRA-HIGH STRENGTH REACTIVE POWDER CONCRETES (MORTARS)

Popis výsledku anglicky

The ultra-high strength of reactive powder concrete (RPC) is achieved due to the following factors very fine aggregate within 0 - 4 mm in size (preferably fused bauxite), proper kind and amount of superplasticizer and steel microfibers and substitution of a part of fine sand by steel powder. The possibility to ensure at least first period of setting under certain pressure is very effective. After 1 day of moist curing at ambient temperature, the compressive strengths exceed 80 MPa. After 28 days they even rise to 220 MPa. Thermal treatment at 250 and 400 causes the formation of crystalline xonotlite and the increase of compressive strengths above 350 MPa, reportedly even above 700 MPa. The study of the further chemical and physico-mechanical propertiesof these very promising high-strength and corrosion resistance performance composites has been in progress.

Druh

D - Stať ve sborníku

CEP obor

CA - Anorganická chemie

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Non-Traditional Cement and Concreta III

ISBN

978-80-214-3642-8

ISSN

—

e-ISSN

—

Počet stran výsledku

4

Strana od-do

—

Název nakladatele

Neuveden

Místo vydání

Brno

Místo konání akce

Brno

Datum konání akce

10. 6. 2008

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—