Dissolving behavior and calcium release from fibrous wollastonite in acetic acid solution
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26310%2F10%3APU88549" target="_blank" >RIV/00216305:26310/10:PU88549 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Dissolving behavior and calcium release from fibrous wollastonite in acetic acid solution
Popis výsledku v původním jazyce
The degradability of fibrous wollastonite (CaSiO3) in an aqueous solution of acetic acid and leaching of Ca2+ ions were investigated in the temperature range from 22 to 50 C. The Inductively Coupled Plasma Atomic Emission Spectroscopy (ICP-OES) was usedfor the assessment of calcium and other selected cations in the leaching medium. The amount of calcium in the solvent can be significantly enhanced through leaching at higher temperature. Fibrous silica particles are the main by-product of the leaching process. The properties of by-product were examined by thermal analysis (simultaneous TG-DTA-EGA), infrared spectroscopy (FT-IR) and scanning electron microscopy (SEM). The formation of silica layer on the surface of fibrous wollastonite particles is an important factor in the leaching process. Particles were covered by the silica layer and wollastonite core size was continually decreasing during leaching. The shape of resulting silica particles shows no significant changes during this pr
Název v anglickém jazyce
Dissolving behavior and calcium release from fibrous wollastonite in acetic acid solution
Popis výsledku anglicky
The degradability of fibrous wollastonite (CaSiO3) in an aqueous solution of acetic acid and leaching of Ca2+ ions were investigated in the temperature range from 22 to 50 C. The Inductively Coupled Plasma Atomic Emission Spectroscopy (ICP-OES) was usedfor the assessment of calcium and other selected cations in the leaching medium. The amount of calcium in the solvent can be significantly enhanced through leaching at higher temperature. Fibrous silica particles are the main by-product of the leaching process. The properties of by-product were examined by thermal analysis (simultaneous TG-DTA-EGA), infrared spectroscopy (FT-IR) and scanning electron microscopy (SEM). The formation of silica layer on the surface of fibrous wollastonite particles is an important factor in the leaching process. Particles were covered by the silica layer and wollastonite core size was continually decreasing during leaching. The shape of resulting silica particles shows no significant changes during this pr
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JP - Průmyslové procesy a zpracování
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/2B08024" target="_blank" >2B08024: Výzkum a vývoj ekologického pojiva na bázi geopolymerních struktur se schopností imobilizace potenciálně nebezpečných látek z velkoobjemově produkovaných průmyslových odpadů a jeho následné aplikace ve stavebnictví</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Thermochimica Acta
ISSN
0040-6031
e-ISSN
—
Svazek periodika
498
Číslo periodika v rámci svazku
1-2
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
7
Strana od-do
—
Kód UT WoS článku
000274948900010
EID výsledku v databázi Scopus
—