Reduction of Brass Model Corrosion Layers Using Low-Pressure Low-Temperature Hydrogen Plasma

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26310%2F13%3APU105270" target="_blank" >RIV/00216305:26310/13:PU105270 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/00216305:26310/13:PU105269
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Reduction of Brass Model Corrosion Layers Using Low-Pressure Low-Temperature Hydrogen Plasma
Popis výsledku v původním jazyce
Brass samples were chosen for plasma chemical reduction of corrosion layers. Model corrosion layers were prepared in two corrosion layers (acidic and alkaline atmosphere) and with/without sand at the sample surface. Samples were treated in low-pressure low-temperature hydrogen plasma for 120 minutes, pressure was about 150 Pa, hydrogen flow 50 sccm. The whole process was monitored by optical emission spectroscopy.
Název v anglickém jazyce
Reduction of Brass Model Corrosion Layers Using Low-Pressure Low-Temperature Hydrogen Plasma
Popis výsledku anglicky
Brass samples were chosen for plasma chemical reduction of corrosion layers. Model corrosion layers were prepared in two corrosion layers (acidic and alkaline atmosphere) and with/without sand at the sample surface. Samples were treated in low-pressure low-temperature hydrogen plasma for 120 minutes, pressure was about 150 Pa, hydrogen flow 50 sccm. The whole process was monitored by optical emission spectroscopy.

Projekt
<a href="/cs/project/DF11P01OVV004" target="_blank" >DF11P01OVV004: Plazmochemické procesy a technologie pro konzervaci kovových archeologických předmětů</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění
2013
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)