Enhanced interfacial adhesion of glass fibers by tetravinylsilane plasma modification

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26310%2F14%3APU112385" target="_blank" >RIV/00216305:26310/14:PU112385 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.compositesa.2013.12.003" target="_blank" >http://dx.doi.org/10.1016/j.compositesa.2013.12.003</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.compositesa.2013.12.003" target="_blank" >10.1016/j.compositesa.2013.12.003</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Enhanced interfacial adhesion of glass fibers by tetravinylsilane plasma modification

Popis výsledku v původním jazyce

Plasma-polymerized tetravinylsilane was used to surface modify glass fibers to improve interfacial adhesion of a GF/polyester composite. Plasma polymer films of controllable thickness and physicochemical properties were deposited on unsized glass fibers by RF pulsed plasma using an effective power of 0.1 – 5 W. The interfacial adhesion of unsized, industrially sized, oxygen plasma treated, and plasma polymer coated fibers embedded in polyester resin was determined by microindentation. The plasma modification of the glass fibers enabled a considerable increase in the interfacial shear strength compared to unsized fibers. The interfacial shear strength for the optimized plasma coating was 26% higher than that for the industrial sizing.

Název v anglickém jazyce

Enhanced interfacial adhesion of glass fibers by tetravinylsilane plasma modification

Popis výsledku anglicky

Plasma-polymerized tetravinylsilane was used to surface modify glass fibers to improve interfacial adhesion of a GF/polyester composite. Plasma polymer films of controllable thickness and physicochemical properties were deposited on unsized glass fibers by RF pulsed plasma using an effective power of 0.1 – 5 W. The interfacial adhesion of unsized, industrially sized, oxygen plasma treated, and plasma polymer coated fibers embedded in polyester resin was determined by microindentation. The plasma modification of the glass fibers enabled a considerable increase in the interfacial shear strength compared to unsized fibers. The interfacial shear strength for the optimized plasma coating was 26% higher than that for the industrial sizing.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20505 - Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics; filled composites)

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING

ISSN

1359-835X

e-ISSN

1878-5840

Svazek periodika

58

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

6

Strana od-do

84-89

Kód UT WoS článku

000331161900012

EID výsledku v databázi Scopus

2-s2.0-84891817041