STUDY OF HYDRATION PRODUCTS IN THE MODEL SYSTEMS METAKAOLIN?LIME AND METAKAOLIN?LIME?GYPSUM
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26310%2F15%3APU118475" target="_blank" >RIV/00216305:26310/15:PU118475 - isvavai.cz</a>
Výsledek na webu
<a href="http://www.ceramics-silikaty.cz/2015/pdf/2015_04_283.pdf" target="_blank" >http://www.ceramics-silikaty.cz/2015/pdf/2015_04_283.pdf</a>
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
STUDY OF HYDRATION PRODUCTS IN THE MODEL SYSTEMS METAKAOLIN?LIME AND METAKAOLIN?LIME?GYPSUM
Popis výsledku v původním jazyce
Possible preferential formation of ettringite instead of required calcium silicate hydrate (CSH) and calcium aluminosilicate hydrate (CASH) phases when aluminosilicates were added to the blended cements was investigated on the model systems comprising ofmetakaolin, lime and gypsum. Compressive strength, microstructure and phase composition of the samples were evaluated after 7 days of curing at 50°C, using thermal analysis, X-ray diffraction techniques and scanning electronic microscopy. Samples prepared from equal amounts of metakaolin, lime and with more than 8 wt. % of gypsum, displayed the highest compressive strength values. Development of compressive strength was correlated with the formation of ettringite. Further rising of gypsum content resulted in the decrease of compressive strength, which is notable in the samples with a different metakaolin/lime ratio. Lower content of gypsum led to the preferential formation of portlandite, CSH and CASH. Calcite was detected in all the s
Název v anglickém jazyce
STUDY OF HYDRATION PRODUCTS IN THE MODEL SYSTEMS METAKAOLIN?LIME AND METAKAOLIN?LIME?GYPSUM
Popis výsledku anglicky
Possible preferential formation of ettringite instead of required calcium silicate hydrate (CSH) and calcium aluminosilicate hydrate (CASH) phases when aluminosilicates were added to the blended cements was investigated on the model systems comprising ofmetakaolin, lime and gypsum. Compressive strength, microstructure and phase composition of the samples were evaluated after 7 days of curing at 50°C, using thermal analysis, X-ray diffraction techniques and scanning electronic microscopy. Samples prepared from equal amounts of metakaolin, lime and with more than 8 wt. % of gypsum, displayed the highest compressive strength values. Development of compressive strength was correlated with the formation of ettringite. Further rising of gypsum content resulted in the decrease of compressive strength, which is notable in the samples with a different metakaolin/lime ratio. Lower content of gypsum led to the preferential formation of portlandite, CSH and CASH. Calcite was detected in all the s
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JJ - Ostatní materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/LO1211" target="_blank" >LO1211: Centrum materiálového výzkumu na FCH VUT v Brně - udržitelnost a rozvoj</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Ceramics-Silikáty
ISSN
0862-5468
e-ISSN
—
Svazek periodika
4
Číslo periodika v rámci svazku
59
Stát vydavatele periodika
CZ - Česká republika
Počet stran výsledku
9
Strana od-do
283-291
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—