Characterization of Ni-P coating prepared on wrought AZ61 magnesium alloy via electroless deposition

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26310%2F17%3APU124818" target="_blank" >RIV/00216305:26310/17:PU124818 - isvavai.cz</a>

Výsledek na webu

<a href="https://apps.webofknowledge.com/full_record.do?product=WOS&search_mode=GeneralSearch&qid=4&SID=D1NKOwzfyrTN8G7nNEU&page=1&doc=3" target="_blank" >https://apps.webofknowledge.com/full_record.do?product=WOS&search_mode=GeneralSearch&qid=4&SID=D1NKOwzfyrTN8G7nNEU&page=1&doc=3</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.17222/mit.2017.029" target="_blank" >10.17222/mit.2017.029</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Characterization of Ni-P coating prepared on wrought AZ61 magnesium alloy via electroless deposition

Popis výsledku v původním jazyce

Low phosphorous Ni-P coating was prepared on wrought AZ61 magnesium alloy via electroless deposition for 1 hour after adequate substrate surface pre-treatment. Prepared coating with the thickness of 10 µm was characterized by uniform distribution of Ni (95.4 wt. %) and P (4.6 wt. %) in the cross-section. Microcavities present in the coating resulted in the quite low corrosion resistance of the coated magnesium alloy in 0.1 M NaCl solution. On the other hand, the coating exhibits a high degree of adhesion, as evidenced by scratch test, and significantly improves AZ61 magnesium alloy microhardness (from 79 ± 6 HV 0.025 to 700 ± 40HV 0.025).

Název v anglickém jazyce

Characterization of Ni-P coating prepared on wrought AZ61 magnesium alloy via electroless deposition

Popis výsledku anglicky

Low phosphorous Ni-P coating was prepared on wrought AZ61 magnesium alloy via electroless deposition for 1 hour after adequate substrate surface pre-treatment. Prepared coating with the thickness of 10 µm was characterized by uniform distribution of Ni (95.4 wt. %) and P (4.6 wt. %) in the cross-section. Microcavities present in the coating resulted in the quite low corrosion resistance of the coated magnesium alloy in 0.1 M NaCl solution. On the other hand, the coating exhibits a high degree of adhesion, as evidenced by scratch test, and significantly improves AZ61 magnesium alloy microhardness (from 79 ± 6 HV 0.025 to 700 ± 40HV 0.025).

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20506 - Coating and films

Projekt

<a href="/cs/project/LO1211" target="_blank" >LO1211: Centrum materiálového výzkumu na FCH VUT v Brně - udržitelnost a rozvoj</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materiali in tehnologije

ISSN

1580-2949

e-ISSN

1580-3414

Svazek periodika

51

Číslo periodika v rámci svazku

6

Stát vydavatele periodika

SI - Slovinská republika

Počet stran výsledku

7

Strana od-do

925-931

Kód UT WoS článku

000418289300007

EID výsledku v databázi Scopus

2-s2.0-85040941664