The influence of different starting conditions to the hydrothermal formation of tobermorite - influence of silica source and water-to-solid ratio

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26310%2F19%3APU132454" target="_blank" >RIV/00216305:26310/19:PU132454 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

The influence of different starting conditions to the hydrothermal formation of tobermorite - influence of silica source and water-to-solid ratio

Popis výsledku v původním jazyce

In this study, the influence of different starting materials, especially the silica source was studied. Hydrothermal reactions were performed at 180 °C under saturated steam pressure, while the reaction time was three days and C/S ratio of the starting mixture was set to 0.83. For the synthesis of tobermorite, the crystalline silica source with finer particles is favourable. After three days of reaction using silica sand Dorsilit (d50 = 5.3 µm) and w/s ratio in the range 2–5 ml/g tobermorite is the main detected phase in the samples. When amorphous silica sources (industrially prepared micro silica and self-synthesised SixOyOHz from TEOS) were used as starting materials, other C–S–H phases like gyrolite, hillebrandite and clinotobermorite were prepared.

Název v anglickém jazyce

The influence of different starting conditions to the hydrothermal formation of tobermorite - influence of silica source and water-to-solid ratio

Popis výsledku anglicky

In this study, the influence of different starting materials, especially the silica source was studied. Hydrothermal reactions were performed at 180 °C under saturated steam pressure, while the reaction time was three days and C/S ratio of the starting mixture was set to 0.83. For the synthesis of tobermorite, the crystalline silica source with finer particles is favourable. After three days of reaction using silica sand Dorsilit (d50 = 5.3 µm) and w/s ratio in the range 2–5 ml/g tobermorite is the main detected phase in the samples. When amorphous silica sources (industrially prepared micro silica and self-synthesised SixOyOHz from TEOS) were used as starting materials, other C–S–H phases like gyrolite, hillebrandite and clinotobermorite were prepared.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20101 - Civil engineering

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2019

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

15th International Congress on the Chemistry of Cement (ICCC 2019) Congress proceedings – Papers and Posters Proceedings

ISBN

—

ISSN

2523-935X

e-ISSN

—

Počet stran výsledku

11

Strana od-do

1-11

Název nakladatele

Research Institute of Binding Materials Prague

Místo vydání

Praha

Místo konání akce

Praha

Datum konání akce

16. 9. 2019

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—