MICROSTRUCTURAL CHARACTERIZATION AND WEAR BEHAVIOR OF WC-COCR COATING ON AZ91 MAGNESIUM ALLOY

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26310%2F19%3APU133917" target="_blank" >RIV/00216305:26310/19:PU133917 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

MICROSTRUCTURAL CHARACTERIZATION AND WEAR BEHAVIOR OF WC-COCR COATING ON AZ91 MAGNESIUM ALLOY

Popis výsledku v původním jazyce

This paper includes the microstructural and wear characterization of WC-10Co4Cr coating on AZ91 magnesium alloy. Using the scanning electron microscopy and X-ray diffraction analysis it was determined that the microstructure was formed by WC particles, CoCr matrix, present Co3W3C mixed carbide, W2C, and free carbon. The presence of W2C and free carbon indicates the partial decarburization during the spraying process. The microhardness of HVOF-sprayed coating was 1480 ± 80 HV 0.05, which is approximately 20× higher when compared to AZ91 alloy. The friction coefficient values with the subsequent weight loss of the coating and magnesium substrate were determined. It has been proven that HVOF-sprayed WC-CoCr coating can protect the magnesium substrate from the wear.

Název v anglickém jazyce

MICROSTRUCTURAL CHARACTERIZATION AND WEAR BEHAVIOR OF WC-COCR COATING ON AZ91 MAGNESIUM ALLOY

Popis výsledku anglicky

This paper includes the microstructural and wear characterization of WC-10Co4Cr coating on AZ91 magnesium alloy. Using the scanning electron microscopy and X-ray diffraction analysis it was determined that the microstructure was formed by WC particles, CoCr matrix, present Co3W3C mixed carbide, W2C, and free carbon. The presence of W2C and free carbon indicates the partial decarburization during the spraying process. The microhardness of HVOF-sprayed coating was 1480 ± 80 HV 0.05, which is approximately 20× higher when compared to AZ91 alloy. The friction coefficient values with the subsequent weight loss of the coating and magnesium substrate were determined. It has been proven that HVOF-sprayed WC-CoCr coating can protect the magnesium substrate from the wear.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20506 - Coating and films

Projekt

<a href="/cs/project/LO1211" target="_blank" >LO1211: Centrum materiálového výzkumu na FCH VUT v Brně - udržitelnost a rozvoj</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2019

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2019, May 22 nd - 24 th 2019, Conference Proceedings

ISBN

978-80-87294-92-5

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

922-927

Název nakladatele

TANGER Ltd.

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

22. 5. 2019

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

000539487400150