ZE10 MAGNESIUM ALLOY CORROSION PROPERTIES IMPROVEMENT BY UNCONVENTIONAL FLUORIDE CONVERSION COATING
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26310%2F19%3APU134541" target="_blank" >RIV/00216305:26310/19:PU134541 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
ZE10 MAGNESIUM ALLOY CORROSION PROPERTIES IMPROVEMENT BY UNCONVENTIONAL FLUORIDE CONVERSION COATING
Popis výsledku v původním jazyce
The paper offers an analysis of the fluoride conversion coating prepared on ZE10 magnesium alloy with the aim to improve material corrosion properties with respect to the biocompatibility of the alloy. The coating was prepared via unconventional process, by immersion of the alloy in Na[BF4] molten salt at 430 and 450 °C for various treatment times. The coating was analysed in terms of scanning electron microscopy, energy dispersive X-ray spectroscopy and electrochemical impedance spectroscopy. The coating was shown to be compact and homogenous with intermetallic particles incorporated in the coating. Significantly higher values of the polarization resistance were estimated for the coated specimens when compared to the untreated ZE10 alloy in simulated body fluid solution at 37 ± 2 °C.
Název v anglickém jazyce
ZE10 MAGNESIUM ALLOY CORROSION PROPERTIES IMPROVEMENT BY UNCONVENTIONAL FLUORIDE CONVERSION COATING
Popis výsledku anglicky
The paper offers an analysis of the fluoride conversion coating prepared on ZE10 magnesium alloy with the aim to improve material corrosion properties with respect to the biocompatibility of the alloy. The coating was prepared via unconventional process, by immersion of the alloy in Na[BF4] molten salt at 430 and 450 °C for various treatment times. The coating was analysed in terms of scanning electron microscopy, energy dispersive X-ray spectroscopy and electrochemical impedance spectroscopy. The coating was shown to be compact and homogenous with intermetallic particles incorporated in the coating. Significantly higher values of the polarization resistance were estimated for the coated specimens when compared to the untreated ZE10 alloy in simulated body fluid solution at 37 ± 2 °C.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20506 - Coating and films
Návaznosti výsledku
Projekt
<a href="/cs/project/LO1211" target="_blank" >LO1211: Centrum materiálového výzkumu na FCH VUT v Brně - udržitelnost a rozvoj</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2019
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
METAL 2019, May 22 nd - 24 th 2019, Conference Proceedings
ISBN
978-80-87294-92-5
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
897-902
Název nakladatele
TANGER Ltd.
Místo vydání
Ostrava
Místo konání akce
Brno
Datum konání akce
22. 5. 2019
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000539487400146