Corrosion resistance of the biodegradable ZE41 magnesium alloy treated by unconventional fluoride conversion coating

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26310%2F19%3APU144067" target="_blank" >RIV/00216305:26310/19:PU144067 - isvavai.cz</a>

Výsledek na webu

<a href="https://www.sciendo.com/article/10.2478/kom-2019-0018" target="_blank" >https://www.sciendo.com/article/10.2478/kom-2019-0018</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.2478/kom-2019-0018" target="_blank" >10.2478/kom-2019-0018</a>

Jazyk výsledku

slovinština

Název v původním jazyce

Korózna odolnosť biologicky odbúrateľnej horčíkovej zliatiny ZE41 upravenej nekonvenčným fluoridovým konverzným povlakom

Popis výsledku v původním jazyce

Horčíkové zliatiny predstavujú perspektívne materiály využiteľné v medicínskych aplikáciách, a to predovšetkým ako biologicky odbúrateľné implantáty. Avšak pre ich nízku koróznu odolnosť v prostredí in vivo, je ich využitie výrazne limitované. Zvýšenie koróznej odolnosti horčíkových zliatin v prostredí in vivo je možné docieliť napríklad vhodnou voľbou povrchovej úpravy za súčasného zabezpečenia podmienky biokompatibility. Fluoridové konverzné povlaky uvedené kritériá spĺňajú. Na horčíkovej zliatine ZE41 bol nekonvenčnou technológiou pripravený fluoridový konverzný povlak, a to vložením horčíkovej zliatiny do roztavenej soli Na[BF4] pri teplote 450 °C a čase ponorenia 0,5; 2 a 8 h. Na takto pripravených vzorkách bola skúmaná morfológia a hrúbka pripraveného povlaku, ako aj korózna odolnosť vzoriek bez a s fluoridovým konverzným povlakom. Odolnosť proti korózii bola posudzovaná pomocou elektrochemickej impedančnej spektroskopie v prostredí simulovaných telesných tekutín pri teplote 37 ± 2 °C. Získané výsledky ukázali, že vzorky s takto pripravenými fluoridovými konverznými povlakmi vykazujú výrazné zvýšenie koróznej odolnosti v porovnaní so vzorkami horčíkovej zliatiny ZE41 bez fluoridového konverzného povlaku.

Název v anglickém jazyce

Corrosion resistance of the biodegradable ZE41 magnesium alloy treated by unconventional fluoride conversion coating

Popis výsledku anglicky

Magnesium based alloys are very promising material to be used mainly for biodegradable implants in medical applications. However, due to their very low corrosion resistance in the environment of in vivo is their use limited. Increase of the corrosion resistance of magnesium alloys in vivo can be achieved, for example, by a suitable choice of surface treatment while the biocompatibility must be ensured. Fluoride conversion coatings meet these requirements. Unconventional fluoride conversion coating was prepared on ZE41 magnesium alloy by dipping the magnesium alloy into the Na[BF4] salt melt at 450 °C for 0.5; 2 and 8 h. The morphology and thickness of the prepared fluoride conversion coatings were investigated as well as the corrosion resistance of the treated and untreated ZE41 magnesium alloy specimens. The corrosion resistance of the untreated and treated ZE41 magnesium alloy was investigated using electrochemical impedance spectroscopy in the environment of the simulated body fluids at 37 ± 2 °C. The obtained results showed a positive influence of the fluoride conversion coating on the corrosion resistance of the ZE41 magnesium alloy.

Druh

J_SC - Článek v periodiku v databázi SCOPUS

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2019

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Koroze a ochrana materiálů

ISSN

0452-599X

e-ISSN

—

Svazek periodika

63

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

10

Strana od-do

138-147

Kód UT WoS článku

—

EID výsledku v databázi Scopus

2-s2.0-85079630801