Supersulphated cements from waste materials
Popis výsledku v původním jazyce
Supersulphated cements are considered to be one of the first alkali-activated cements. Ground granulated blast-furnace slag is activated with a small amount of Portland cement in the presence of gypsum, providing C-S-H gel and ettringite as the main reaction products. These materials exhibit some good properties; the most important of these being good sulphate resistance and also good environmental effects. Standard EN15743+A1 "Supersulphated cement" describes the conditions for the composition of this binder. In this paper, the product after desulphurisation (PPR) from the Třebovice heating plant (Ostrava) was used as a source of gypsum. Strength development was recorded up to 91 days for different ratios of compounds. Early strengths are very low and are higher for higher ordinary Portland cement content. At 28 and 91 days of age the strengths are almost the same for gypsum contents from 10 to 20% and all cement contents (2.5, 3.75% and 5%). These strengths are relatively high - around 50 MPa. Supersulphated cements can be a good choice for the use of waste material - the product after desulphurisation.
Název v anglickém jazyce
Supersulphated cements from waste materials
Popis výsledku anglicky
Supersulphated cements are considered to be one of the first alkali-activated cements. Ground granulated blast-furnace slag is activated with a small amount of Portland cement in the presence of gypsum, providing C-S-H gel and ettringite as the main reaction products. These materials exhibit some good properties; the most important of these being good sulphate resistance and also good environmental effects. Standard EN15743+A1 "Supersulphated cement" describes the conditions for the composition of this binder. In this paper, the product after desulphurisation (PPR) from the Třebovice heating plant (Ostrava) was used as a source of gypsum. Strength development was recorded up to 91 days for different ratios of compounds. Early strengths are very low and are higher for higher ordinary Portland cement content. At 28 and 91 days of age the strengths are almost the same for gypsum contents from 10 to 20% and all cement contents (2.5, 3.75% and 5%). These strengths are relatively high - around 50 MPa. Supersulphated cements can be a good choice for the use of waste material - the product after desulphurisation.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20101 - Civil engineering
Návaznosti výsledku
Projekt
—
Návaznosti
S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2022
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
SP-355: Recent Advances in Concrete Technology and Sustainability Issues
ISBN
978-1-64195-184-5
ISSN
0193-2527
e-ISSN
—
Počet stran výsledku
8
Strana od-do
375-382
Název nakladatele
American Concrete Institute
Místo vydání
Milán
Místo konání akce
Milán
Datum konání akce
13. 7. 2022
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—