Měření elektrokinetického potenciálu v soustavě SiO2-CaCl2-H2O.

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26310%2F99%3APU38347" target="_blank" >RIV/00216305:26310/99:PU38347 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Electrokinetic Potential Measurements In A System Of Silicon dioxide-Calcium Chloride and Water

Popis výsledku v původním jazyce

The aim of the presented work was to study the dependence of the SiO2 sol zeta potential on the contents of calcium chloride. The sol contained 2.27 wt. % of SiO2 and the content of anhydrous CaCl2 varied between 0.126 and 13.0 wt. %. The experiments demonstrated an influence of calcium and chloride ions on the electrokinetic potential. Formation of gels based on calcium-silicate hydrates can be expected with an increasing content of calcium ions in the solution. On the other hand, increasing content off chloride ions brings about a lowering of the pH of the solution, thus slowing down the transport of the silicate components into the solution. These chloride effects are more apparent at higher CaCl2 concentrations. The described phenomenon explains the behaviour of calcium chloride as an additive accelerating the hydration of the silicate components of clinker minerals.

Název v anglickém jazyce

Electrokinetic Potential Measurements In A System Of Silicon dioxide-Calcium Chloride and Water

Popis výsledku anglicky

The aim of the presented work was to study the dependence of the SiO2 sol zeta potential on the contents of calcium chloride. The sol contained 2.27 wt. % of SiO2 and the content of anhydrous CaCl2 varied between 0.126 and 13.0 wt. %. The experiments demonstrated an influence of calcium and chloride ions on the electrokinetic potential. Formation of gels based on calcium-silicate hydrates can be expected with an increasing content of calcium ions in the solution. On the other hand, increasing content off chloride ions brings about a lowering of the pH of the solution, thus slowing down the transport of the silicate components into the solution. These chloride effects are more apparent at higher CaCl2 concentrations. The described phenomenon explains the behaviour of calcium chloride as an additive accelerating the hydration of the silicate components of clinker minerals.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

CF - Fyzikální chemie a teoretická chemie

OECD FORD obor

—

Projekt

<a href="/cs/project/GA203%2F94%2F1568" target="_blank" >GA203/94/1568: Hydratované materiály, chemismus procesu tuhnutí a tvrdnutí.</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

1999

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Ceramics-Silikáty

ISSN

0862-5468

e-ISSN

—

Svazek periodika

43

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

5

Strana od-do

18-22

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—