Experimental Investigation of Modes II and III Fatigue Crack Growth in Unalloyed Titanium
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F14%3APU106478" target="_blank" >RIV/00216305:26620/14:PU106478 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.592-593.797" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/KEM.592-593.797</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.592-593.797" target="_blank" >10.4028/www.scientific.net/KEM.592-593.797</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Experimental Investigation of Modes II and III Fatigue Crack Growth in Unalloyed Titanium
Popis výsledku v původním jazyce
The study is focused on finding and describing microscopic paths of modes II and III cracks in commercially pure titanium. Experiments were done on cylindrical bars with a circumferential cracked notch loaded in shear (modes II, III and II + III) and torsion (mode III). Fractography analysis showed that the crack growth was crystallography-controlled and the deflection and twisting angles of crack propagation direction (with respect to the shear plane) were relatively high. This behavior can be understood in terms of available slip systems in bcc, fcc and hcp lattices.
Název v anglickém jazyce
Experimental Investigation of Modes II and III Fatigue Crack Growth in Unalloyed Titanium
Popis výsledku anglicky
The study is focused on finding and describing microscopic paths of modes II and III cracks in commercially pure titanium. Experiments were done on cylindrical bars with a circumferential cracked notch loaded in shear (modes II, III and II + III) and torsion (mode III). Fractography analysis showed that the crack growth was crystallography-controlled and the deflection and twisting angles of crack propagation direction (with respect to the shear plane) were relatively high. This behavior can be understood in terms of available slip systems in bcc, fcc and hcp lattices.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20306 - Audio engineering, reliability analysis
Návaznosti výsledku
Projekt
<a href="/cs/project/GAP107%2F12%2F0800" target="_blank" >GAP107/12/0800: Únava aktuátorů z vysokoteplotních slitin s tvarovou pamětí NiTiX /FACT/</a><br>
Návaznosti
S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Key Engineering Materials (print)
ISSN
1013-9826
e-ISSN
—
Svazek periodika
592-593
Číslo periodika v rámci svazku
797-800
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
4
Strana od-do
797-800
Kód UT WoS článku
000336694400183
EID výsledku v databázi Scopus
2-s2.0-84891886292