Specimens for Simultaneous Mode II, III and II+III Fatigue Crack Propagation: Elasto-Plastic Solution of Crack Tip Stress-Strain Field
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F14%3APU108338" target="_blank" >RIV/00216305:26620/14:PU108338 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.4028/www.scientific.net/AMR.891-892.1585" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/AMR.891-892.1585</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/AMR.891-892.1585" target="_blank" >10.4028/www.scientific.net/AMR.891-892.1585</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Specimens for Simultaneous Mode II, III and II+III Fatigue Crack Propagation: Elasto-Plastic Solution of Crack Tip Stress-Strain Field
Popis výsledku v původním jazyce
Determination of fatigue crack growth characteristics under shear-mode loading is a rather complicated problem. To increase an efficiency and precision of such testing, special specimens enabling simultaneous propagation of shear cracks under II, III andII+III loading modes started to be used rather recently. K-calibration of these specimens was performed and, after unique pre-crack and heat-treatment procedures, effective thresholds KII eff;th and KIII eff;th in several metallic materials could be measured. However, a description of crack growth rate in terms of appropriate fracture mechanics quantities demands a precise assessment of plastic zone size under various shear-mode loading levels. This contribution is focused on the numerical elasto-plastic analysis of stress-strain field at the crack tip in specimens made of a pure polycrystalline (ARMCO) iron. The results reveal that the small scale yielding conditions are fulfilled in the near-threshold region. Starting from K values h
Název v anglickém jazyce
Specimens for Simultaneous Mode II, III and II+III Fatigue Crack Propagation: Elasto-Plastic Solution of Crack Tip Stress-Strain Field
Popis výsledku anglicky
Determination of fatigue crack growth characteristics under shear-mode loading is a rather complicated problem. To increase an efficiency and precision of such testing, special specimens enabling simultaneous propagation of shear cracks under II, III andII+III loading modes started to be used rather recently. K-calibration of these specimens was performed and, after unique pre-crack and heat-treatment procedures, effective thresholds KII eff;th and KIII eff;th in several metallic materials could be measured. However, a description of crack growth rate in terms of appropriate fracture mechanics quantities demands a precise assessment of plastic zone size under various shear-mode loading levels. This contribution is focused on the numerical elasto-plastic analysis of stress-strain field at the crack tip in specimens made of a pure polycrystalline (ARMCO) iron. The results reveal that the small scale yielding conditions are fulfilled in the near-threshold region. Starting from K values h
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
11TH INTERNATIONAL FATIGUE CONGRESS
ISBN
978-3-03835-008-8
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
1585-1590
Název nakladatele
Trans Tech Publications
Místo vydání
Melbourne
Místo konání akce
Melbourne
Datum konání akce
3. 3. 2014
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000337767700245