Failure Analysis of Spherical Roller Bearing

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F14%3APU108561" target="_blank" >RIV/00216305:26620/14:PU108561 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.scientific.net/MSF.782.247" target="_blank" >http://www.scientific.net/MSF.782.247</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.4028/www.scientific.net/MSF.782.247" target="_blank" >10.4028/www.scientific.net/MSF.782.247</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Failure Analysis of Spherical Roller Bearing

Popis výsledku v původním jazyce

The failure of a spherical-roller bearing consisting of spherical rollers, outer and inner rings made of 100CrMn6 steel was studied. After a trial test, in which several spherical rollers were completely destroyed and a long continuous radial crack appeared in the outer ring, pitting degradation was observed on all bearing parts. The bearing components were studied (separately) by means of light and electron microscopy. The chemical composition was estimated by means of glow discharge optical emission spectroscopy. X-ray diffraction was utilized for qualitative and quantitative phase analyses. As a representative of mechanical properties, the hardness was also measured.

Název v anglickém jazyce

Failure Analysis of Spherical Roller Bearing

Popis výsledku anglicky

The failure of a spherical-roller bearing consisting of spherical rollers, outer and inner rings made of 100CrMn6 steel was studied. After a trial test, in which several spherical rollers were completely destroyed and a long continuous radial crack appeared in the outer ring, pitting degradation was observed on all bearing parts. The bearing components were studied (separately) by means of light and electron microscopy. The chemical composition was estimated by means of glow discharge optical emission spectroscopy. X-ray diffraction was utilized for qualitative and quantitative phase analyses. As a representative of mechanical properties, the hardness was also measured.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Metallography XV

ISBN

978-3-03835-072-9

ISSN

0255-5476

e-ISSN

—

Počet stran výsledku

4

Strana od-do

247-250

Název nakladatele

Trans Tech Publication

Místo vydání

Switzerland

Místo konání akce

Stará Lesná

Datum konání akce

24. 4. 2013

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

000338978600044