Comparative Analysis of Hard Anodized Layer on Aluminium Alloy
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F14%3APU108563" target="_blank" >RIV/00216305:26620/14:PU108563 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.4028/www.scientific.net/MSF.782/615" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/MSF.782/615</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/MSF.782/615" target="_blank" >10.4028/www.scientific.net/MSF.782/615</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Comparative Analysis of Hard Anodized Layer on Aluminium Alloy
Popis výsledku v původním jazyce
Hard anodized layers were produced by two different manufacturers on the same type of aluminium alloy and the complex in-shape vacuum pump part. The sulphuric acid/water solution was used for alumina layers formation, which were subsequently sealed in demineralized water. Comparative analysis based on metallographic methodology, with the aim to control the stability of alumina formation process and to identify its defects, was performed by means of light and scanning electron microscopy, surface profilometry and microhardness measurements. To determine the thicknesses of alumina layers, the image analysis was also used.
Název v anglickém jazyce
Comparative Analysis of Hard Anodized Layer on Aluminium Alloy
Popis výsledku anglicky
Hard anodized layers were produced by two different manufacturers on the same type of aluminium alloy and the complex in-shape vacuum pump part. The sulphuric acid/water solution was used for alumina layers formation, which were subsequently sealed in demineralized water. Comparative analysis based on metallographic methodology, with the aim to control the stability of alumina formation process and to identify its defects, was performed by means of light and scanning electron microscopy, surface profilometry and microhardness measurements. To determine the thicknesses of alumina layers, the image analysis was also used.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/ED1.1.00%2F02.0068" target="_blank" >ED1.1.00/02.0068: CEITEC - central european institute of technology</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Metallography XV
ISBN
978-3-03835-072-9
ISSN
0255-5476
e-ISSN
—
Počet stran výsledku
4
Strana od-do
615-618
Název nakladatele
Trans Tech Publication
Místo vydání
Switzerland
Místo konání akce
Stará Lesná
Datum konání akce
24. 4. 2013
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—