Analysis of Post-Machining Defects in AlSi7Mg0.6 Alloy Castings

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F14%3APU109731" target="_blank" >RIV/00216305:26620/14:PU109731 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Analysis of Post-Machining Defects in AlSi7Mg0.6 Alloy Castings
Popis výsledku v původním jazyce
Via visual checking and metallographic analysis, local deformations in the shape of bulges with cracks were identified on the machined inner wall of aluminium alloy castings. These defects appeared due to foundry defects on the opposite outer wall of thecasting being repaired by welding and to the subsequent release of internal stress after the inner wall of the casting was machined.
Název v anglickém jazyce
Analysis of Post-Machining Defects in AlSi7Mg0.6 Alloy Castings
Popis výsledku anglicky
Via visual checking and metallographic analysis, local deformations in the shape of bulges with cracks were identified on the machined inner wall of aluminium alloy castings. These defects appeared due to foundry defects on the opposite outer wall of thecasting being repaired by welding and to the subsequent release of internal stress after the inner wall of the casting was machined.

Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)