Transparent Tetragonal Zirconia Ceramics by Colloidal Processing of Nanoparticle Suspension

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F14%3APU112456" target="_blank" >RIV/00216305:26620/14:PU112456 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.scientific.net" target="_blank" >http://www.scientific.net</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.4028/www.scientific.net/AST.87.85" target="_blank" >10.4028/www.scientific.net/AST.87.85</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Transparent Tetragonal Zirconia Ceramics by Colloidal Processing of Nanoparticle Suspension

Popis výsledku v původním jazyce

Colloidal processing was applied to a commercial 5 vol% 3Y-ZrO2 nanosuspension with a particle size of 10-15 nm. The nanosuspension was concentrated by evaporation or by the newly developed method of osmotic dehydration. The viscosity and stability of concentrated suspensions were investigated. The concentrated nanosuspension prepared by osmotic dehydration was consolidated by centrifugation in non-porous moulds. The dried deposit had a relative density of 46% and pores ranged from 4 to 8 nm. This deposit was densified by pressureless presintering to closed porosity, followed by hot isostatic pressing in order to obtain transparent ceramics. After sintering, the tetragonal zirconia retained the nanocrystalline structure with an average grain size of 65nm and an in-line transmission of 25 % (at 633 nm wavelength and 0.5 mm plate thickness).

Název v anglickém jazyce

Transparent Tetragonal Zirconia Ceramics by Colloidal Processing of Nanoparticle Suspension

Popis výsledku anglicky

Colloidal processing was applied to a commercial 5 vol% 3Y-ZrO2 nanosuspension with a particle size of 10-15 nm. The nanosuspension was concentrated by evaporation or by the newly developed method of osmotic dehydration. The viscosity and stability of concentrated suspensions were investigated. The concentrated nanosuspension prepared by osmotic dehydration was consolidated by centrifugation in non-porous moulds. The dried deposit had a relative density of 46% and pores ranged from 4 to 8 nm. This deposit was densified by pressureless presintering to closed porosity, followed by hot isostatic pressing in order to obtain transparent ceramics. After sintering, the tetragonal zirconia retained the nanocrystalline structure with an average grain size of 65nm and an in-line transmission of 25 % (at 633 nm wavelength and 0.5 mm plate thickness).

Druh

D - Stať ve sborníku

CEP obor

JH - Keramika, žáruvzdorné materiály a skla

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

13th International Ceramics Congress - Part A

ISBN

978-3-03835-299-0

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

85-90

Název nakladatele

Trans Tech Publication

Místo vydání

Zurich, Switzerland

Místo konání akce

Montecatini Terme, Itálie

Datum konání akce

8. 6. 2014

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—