Polycrystalline alumina ceramics doped with nanoparticles for increased transparency

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F15%3APU113302" target="_blank" >RIV/00216305:26620/15:PU113302 - isvavai.cz</a>

Výsledek na webu

<a href="http://dx.doi.org/10.1016/j.jeurceramsoc.2014.09.041" target="_blank" >http://dx.doi.org/10.1016/j.jeurceramsoc.2014.09.041</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.jeurceramsoc.2014.09.041" target="_blank" >10.1016/j.jeurceramsoc.2014.09.041</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Polycrystalline alumina ceramics doped with nanoparticles for increased transparency

Popis výsledku v původním jazyce

Transparent alumina samples were prepared by the gelcasting process followed by pressureless presintering and hot isostatic pressing. Hightransparency was obtained by doping alumina powder with zirconia and spinel nanoparticles. The doping approach enabled accommodating 0.3wt% zirconia and 0.175 wt% spinel nanoparticles without any light scattering. The doping combined with colloidal processing resulted in grainsize refinement in a fully dense microstructure and adequate in-line transmission improvement. The maximum in-line transmission reached 70.4%at a wavelength of 632.8 nm and a sample thickness of 0.8 mm and was at the theoretical maximum in the infrared wavelength range between 2000 and 4000 nm. The presented processing approach featured near-net shape and scale-up capabilities.

Název v anglickém jazyce

Polycrystalline alumina ceramics doped with nanoparticles for increased transparency

Popis výsledku anglicky

Transparent alumina samples were prepared by the gelcasting process followed by pressureless presintering and hot isostatic pressing. Hightransparency was obtained by doping alumina powder with zirconia and spinel nanoparticles. The doping approach enabled accommodating 0.3wt% zirconia and 0.175 wt% spinel nanoparticles without any light scattering. The doping combined with colloidal processing resulted in grainsize refinement in a fully dense microstructure and adequate in-line transmission improvement. The maximum in-line transmission reached 70.4%at a wavelength of 632.8 nm and a sample thickness of 0.8 mm and was at the theoretical maximum in the infrared wavelength range between 2000 and 4000 nm. The presented processing approach featured near-net shape and scale-up capabilities.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20504 - Ceramics

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of the European Ceramic Society

ISSN

0955-2219

e-ISSN

1873-619X

Svazek periodika

35

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

9

Strana od-do

1001-1009

Kód UT WoS článku

000347664500016

EID výsledku v databázi Scopus

2-s2.0-84930623593