Comparative Study of Microstructure and High Temperature Low Cycle Fatigue Behaviour of Nickel Base Superalloys Inconel 713LC and MAR-M247

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F16%3APU121347" target="_blank" >RIV/00216305:26620/16:PU121347 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.scientific.net/KEM.713.86.pdf" target="_blank" >http://www.scientific.net/KEM.713.86.pdf</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.713.86" target="_blank" >10.4028/www.scientific.net/KEM.713.86</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Comparative Study of Microstructure and High Temperature Low Cycle Fatigue Behaviour of Nickel Base Superalloys Inconel 713LC and MAR-M247

Popis výsledku v původním jazyce

The present work is focused on the study of microstructure and low cycle fatigue behavior of the first Generation nickel-base superalloy IN 713LC (low carbon) and its promising second generation successor MAR-M247 HIP (hot isostatic pressing) at 900 °C. Microstructure of both alloys was studied by means of scanning electron microscopy (SEM). The microstructure of both materials is characterized by dendritic grains, carbides and casting defects. Size and morphology of precipitates and casting defects were evaluated. Fractographic observations have been made with the aim to reveal the fatigue crack initiation place and relation to the casting defects and material microstructure. Low cycle fatigue tests were conducted on cylindrical specimens in symmetrical push-pull cycle under strain control with constant total strain amplitude and strain rate at 900 °C in air. Hardening/softening curves, cyclic stress-strain curve and fatigue life data of both materials were obtained. Cyclic stress-strain curve of MAR M247 is shifted approximately to 120 MPa higher stress amplitudes in comparison with IN 713LC. Significantly higher fatigue life of MAR-M247 has been observed in Basquin representation. On the other hand IN 713LC shows prolonged lifetime compared with MAR-M247 in the Coffin-Manson representation. Results obtained from high temperature low cycle fatigue tests are discussed.

Název v anglickém jazyce

Comparative Study of Microstructure and High Temperature Low Cycle Fatigue Behaviour of Nickel Base Superalloys Inconel 713LC and MAR-M247

Popis výsledku anglicky

The present work is focused on the study of microstructure and low cycle fatigue behavior of the first Generation nickel-base superalloy IN 713LC (low carbon) and its promising second generation successor MAR-M247 HIP (hot isostatic pressing) at 900 °C. Microstructure of both alloys was studied by means of scanning electron microscopy (SEM). The microstructure of both materials is characterized by dendritic grains, carbides and casting defects. Size and morphology of precipitates and casting defects were evaluated. Fractographic observations have been made with the aim to reveal the fatigue crack initiation place and relation to the casting defects and material microstructure. Low cycle fatigue tests were conducted on cylindrical specimens in symmetrical push-pull cycle under strain control with constant total strain amplitude and strain rate at 900 °C in air. Hardening/softening curves, cyclic stress-strain curve and fatigue life data of both materials were obtained. Cyclic stress-strain curve of MAR M247 is shifted approximately to 120 MPa higher stress amplitudes in comparison with IN 713LC. Significantly higher fatigue life of MAR-M247 has been observed in Basquin representation. On the other hand IN 713LC shows prolonged lifetime compared with MAR-M247 in the Coffin-Manson representation. Results obtained from high temperature low cycle fatigue tests are discussed.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/GA15-20991S" target="_blank" >GA15-20991S: Plazmová depozice, strukturní a termomechanická stabilita environmentálních bariér</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Advances in Fracture and Damage Mechanics XV

ISBN

978-0-87849-369-2

ISSN

1662-9795

e-ISSN

—

Počet stran výsledku

3

Strana od-do

86-89

Název nakladatele

SloTrans Tech Publications

Místo vydání

Switzerland

Místo konání akce

Dubrovnik

Datum konání akce

19. 9. 2011

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—