Analysis of damage of solder joint of heat exchanger
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F17%3APU124454" target="_blank" >RIV/00216305:26620/17:PU124454 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.4028/www.scientific.net/SSP.270.63" target="_blank" >http://dx.doi.org/10.4028/www.scientific.net/SSP.270.63</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/SSP.270.63" target="_blank" >10.4028/www.scientific.net/SSP.270.63</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Analysis of damage of solder joint of heat exchanger
Popis výsledku v původním jazyce
The paper focus on the metallographic analysis of damaged heat exchanger made of high-alloy austenitic steel by soldering. The object in question is a soldered joint of main mounting plate of the heat exchanger and first heat exchanging plate of it. In this part of the heat exchanger after the vibration and pressure test crack appeared. The subject of the analysis is the evaluation of the microstructure of the solder joint (high-alloy austenitic steel and copper), and evaluation of the appeared crack. The problematic is solved with aid of metallographic analysis of the microstructure of the material, using light microscopy and scanning electron microscopy and the EDS microanalysis of chemical composition.
Název v anglickém jazyce
Analysis of damage of solder joint of heat exchanger
Popis výsledku anglicky
The paper focus on the metallographic analysis of damaged heat exchanger made of high-alloy austenitic steel by soldering. The object in question is a soldered joint of main mounting plate of the heat exchanger and first heat exchanging plate of it. In this part of the heat exchanger after the vibration and pressure test crack appeared. The subject of the analysis is the evaluation of the microstructure of the solder joint (high-alloy austenitic steel and copper), and evaluation of the appeared crack. The problematic is solved with aid of metallographic analysis of the microstructure of the material, using light microscopy and scanning electron microscopy and the EDS microanalysis of chemical composition.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/LQ1601" target="_blank" >LQ1601: CEITEC 2020</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Přínos metalografie pro řešení výrobních problémů
ISBN
978-80-01-06150-3
ISSN
1662-9779
e-ISSN
—
Počet stran výsledku
6
Strana od-do
63-67
Název nakladatele
Trans Tech Publications
Místo vydání
Switzerland
Místo konání akce
Mariánské Lázně
Datum konání akce
6. 6. 2017
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—