Single Beam Laser Remelted Molybdenum Layer on Aluminum Substrate
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F18%3APU124362" target="_blank" >RIV/00216305:26620/18:PU124362 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Single Beam Laser Remelted Molybdenum Layer on Aluminum Substrate
Popis výsledku v původním jazyce
In this article, the reaction and optimal parameters were investigated for molybdenum layers produced on aluminum substrate using single beam ytterbium fiber laser. To produce these layers the molybdenum powder (25-45um in size) was placed on the aluminum sheet substrate and successfully treated – along the entire length with 16 different irradiation modes. The microstructure of the prepared samples of welded joints was observed by using a light microscope and a scanning electron microscope. Reaction between molybdenum powder and aluminum substrate were examined by energy dispersive X-ray analysis (EDX). The evaluation of optimal parameters was determined from appearances of welded joints, namely their heights and depths.
Název v anglickém jazyce
Single Beam Laser Remelted Molybdenum Layer on Aluminum Substrate
Popis výsledku anglicky
In this article, the reaction and optimal parameters were investigated for molybdenum layers produced on aluminum substrate using single beam ytterbium fiber laser. To produce these layers the molybdenum powder (25-45um in size) was placed on the aluminum sheet substrate and successfully treated – along the entire length with 16 different irradiation modes. The microstructure of the prepared samples of welded joints was observed by using a light microscope and a scanning electron microscope. Reaction between molybdenum powder and aluminum substrate were examined by energy dispersive X-ray analysis (EDX). The evaluation of optimal parameters was determined from appearances of welded joints, namely their heights and depths.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20505 - Composites (including laminates, reinforced plastics, cermets, combined natural and synthetic fibre fabrics; filled composites)
Návaznosti výsledku
Projekt
<a href="/cs/project/LQ1601" target="_blank" >LQ1601: CEITEC 2020</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2018
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Metal 2017 Conference Prosceedings
ISBN
978-80-87294-79-6
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
1110-1115
Název nakladatele
TANGER Ltd.
Místo vydání
Ostrava
Místo konání akce
Brno
Datum konání akce
24. 5. 2017
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000434346900177