Ti3C2Tx MXene characterization produced from SHS-ground Ti3AlC2
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F19%3APU134662" target="_blank" >RIV/00216305:26620/19:PU134662 - isvavai.cz</a>
Výsledek na webu
<a href="https://www.sciencedirect.com/science/article/pii/S0264127519305817" target="_blank" >https://www.sciencedirect.com/science/article/pii/S0264127519305817</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.matdes.2019.108143" target="_blank" >10.1016/j.matdes.2019.108143</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Ti3C2Tx MXene characterization produced from SHS-ground Ti3AlC2
Popis výsledku v původním jazyce
MXenes are an emerging family of two-dimensional (2D) early transition metal carbides/nitrides that are produced by selective A-element chemical etching from 3D MAX phase counterpart. Herein we report a low-cost method combining self-propagation high-temperature synthesis (SHS) and grinding to produce Ti3AlC2 precursor and further its usage to obtain Ti3C2Tx MXene. The SHS-ground precursor requires the same etching conditions as pressure-less synthesized precursors to fully etch A-layer and convert the 3D structure into 2D state. The obtained MXenes are atomically-thin flakes with an average lateral size of 1-2 mu m. The room temperature electrical resistivity of Ti3C2Tx based 11 mu m-thick film ranges between 295 and 317 mu Omega.cm. SHS combining with grinding in one step can be considered as a scalable method to MXene synthesis. (C) 2019 Published by Elsevier Ltd.
Název v anglickém jazyce
Ti3C2Tx MXene characterization produced from SHS-ground Ti3AlC2
Popis výsledku anglicky
MXenes are an emerging family of two-dimensional (2D) early transition metal carbides/nitrides that are produced by selective A-element chemical etching from 3D MAX phase counterpart. Herein we report a low-cost method combining self-propagation high-temperature synthesis (SHS) and grinding to produce Ti3AlC2 precursor and further its usage to obtain Ti3C2Tx MXene. The SHS-ground precursor requires the same etching conditions as pressure-less synthesized precursors to fully etch A-layer and convert the 3D structure into 2D state. The obtained MXenes are atomically-thin flakes with an average lateral size of 1-2 mu m. The room temperature electrical resistivity of Ti3C2Tx based 11 mu m-thick film ranges between 295 and 317 mu Omega.cm. SHS combining with grinding in one step can be considered as a scalable method to MXene synthesis. (C) 2019 Published by Elsevier Ltd.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2019
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Materials & Design
ISSN
0264-1275
e-ISSN
1873-4197
Svazek periodika
183
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
7
Strana od-do
108143-108143
Kód UT WoS článku
000490732800066
EID výsledku v databázi Scopus
—