Analysis of Causec of Baby Stroller Construction Damage
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F20%3APU133709" target="_blank" >RIV/00216305:26620/20:PU133709 - isvavai.cz</a>
Výsledek na webu
<a href="https://www.scientific.net/DDF.405.179" target="_blank" >https://www.scientific.net/DDF.405.179</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/DDF.405.179" target="_blank" >10.4028/www.scientific.net/DDF.405.179</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Analysis of Causec of Baby Stroller Construction Damage
Popis výsledku v původním jazyce
The paper deals with the dispute between the manufacturer and the customer over the warranty claim. The object of the dispute is a damaged stroller construction, Al-Mg-Si aluminum weldment with the final surface treatment by anodic oxidation. The aim of the analysis is to clearly identify the cause of the aluminum structure failure using fractographic and metallographic techniques. Visual inspection revealed cracks in all weld joints and the total destruction of the frame in the area of the front hub, see Fig. 1a. In accordance with the classification of defects according to EN ISO 6520-1, numerous defects were found in welded joints.
Název v anglickém jazyce
Analysis of Causec of Baby Stroller Construction Damage
Popis výsledku anglicky
The paper deals with the dispute between the manufacturer and the customer over the warranty claim. The object of the dispute is a damaged stroller construction, Al-Mg-Si aluminum weldment with the final surface treatment by anodic oxidation. The aim of the analysis is to clearly identify the cause of the aluminum structure failure using fractographic and metallographic techniques. Visual inspection revealed cracks in all weld joints and the total destruction of the frame in the area of the front hub, see Fig. 1a. In accordance with the classification of defects according to EN ISO 6520-1, numerous defects were found in welded joints.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/LQ1601" target="_blank" >LQ1601: CEITEC 2020</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2020
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Metallography & Fractography 2019
ISBN
—
ISSN
1662-9507
e-ISSN
—
Počet stran výsledku
6
Strana od-do
179-184
Název nakladatele
Trans Tech Publications Ltd
Místo vydání
Switzerland
Místo konání akce
Nový Smokovec
Datum konání akce
24. 4. 2019
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—