Transparent magnesium aluminate spinel: Effect of critical temperature in two-stage spark plasma sintering
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F20%3APU136388" target="_blank" >RIV/00216305:26620/20:PU136388 - isvavai.cz</a>
Výsledek na webu
<a href="https://www.sciencedirect.com/science/article/pii/S0955221920300923?via%3Dihub" target="_blank" >https://www.sciencedirect.com/science/article/pii/S0955221920300923?via%3Dihub</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.jeurceramsoc.2020.02.012" target="_blank" >10.1016/j.jeurceramsoc.2020.02.012</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Transparent magnesium aluminate spinel: Effect of critical temperature in two-stage spark plasma sintering
Popis výsledku v původním jazyce
The discolouration of magnesium aluminate spinet caused by carbon contamination is a main drawback of fabricating transparent bodies by spark plasma sintering (SPS). In this study, a two-stage heating rate profile was used to produce transparent MgAl2O4 without using sintering aids by SPS at 1250 degrees C. The effect of critical temperature (Tc), at which the heating rate is decreased, on transparency and carbon contamination was investigated: higher critical temperature resulted in higher contamination. Non-uniform densification indicated that fast heating results in a hot-zone formation in the centre of sintered pellets; the higher temperature of centre favoured reaction of graphite die with spinel and formation of disordered carbon structures in residual pores.
Název v anglickém jazyce
Transparent magnesium aluminate spinel: Effect of critical temperature in two-stage spark plasma sintering
Popis výsledku anglicky
The discolouration of magnesium aluminate spinet caused by carbon contamination is a main drawback of fabricating transparent bodies by spark plasma sintering (SPS). In this study, a two-stage heating rate profile was used to produce transparent MgAl2O4 without using sintering aids by SPS at 1250 degrees C. The effect of critical temperature (Tc), at which the heating rate is decreased, on transparency and carbon contamination was investigated: higher critical temperature resulted in higher contamination. Non-uniform densification indicated that fast heating results in a hot-zone formation in the centre of sintered pellets; the higher temperature of centre favoured reaction of graphite die with spinel and formation of disordered carbon structures in residual pores.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20504 - Ceramics
Návaznosti výsledku
Projekt
<a href="/cs/project/LTT18013" target="_blank" >LTT18013: Vývoj funkčních keramických a sklokeramických materiálů ve spolupráci s Centrem excelence FunGlass</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2020
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of the European Ceramic Society
ISSN
0955-2219
e-ISSN
1873-619X
Svazek periodika
40
Číslo periodika v rámci svazku
6
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
9
Strana od-do
2417-2425
Kód UT WoS článku
000518878300020
EID výsledku v databázi Scopus
2-s2.0-85079119718