Exfoliation of hexagonal boron nitride nanosheets in low-modulus concentrated alkali silicate pastes

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F21%3APU142259" target="_blank" >RIV/00216305:26620/21:PU142259 - isvavai.cz</a>

Výsledek na webu

<a href="https://www.sciencedirect.com/science/article/pii/S0167577X21002470?via%3Dihub" target="_blank" >https://www.sciencedirect.com/science/article/pii/S0167577X21002470?via%3Dihub</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.matlet.2021.129551" target="_blank" >10.1016/j.matlet.2021.129551</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Exfoliation of hexagonal boron nitride nanosheets in low-modulus concentrated alkali silicate pastes

Popis výsledku v původním jazyce

We herein demonstrated the exfoliation of hexagonal boron nitride (h-BN) into nanosheets (BNNSs) by using concentrated low-modulus water glass (WG, SiO2/Na2O ratio = 1.6) as high viscosity exfoliating medium. The process led to BNNSs yield of nearly 30%. As the sheared suspension was neutralized with HCl, BNNSs with lateral size of approximately 250 nm and narrow size distribution, were found to align into perfectly parallel rows. High-resolution transmission electron microscopy (HR-TEM) analysis confirmed how WG preserved the integrity of the exfoliated BNNS in comparison with an analogous route with sole hydroxide, resulting in a high amount of BNNSs with undamaged structure. (C) 2021 Published by Elsevier B.V.

Název v anglickém jazyce

Exfoliation of hexagonal boron nitride nanosheets in low-modulus concentrated alkali silicate pastes

Popis výsledku anglicky

We herein demonstrated the exfoliation of hexagonal boron nitride (h-BN) into nanosheets (BNNSs) by using concentrated low-modulus water glass (WG, SiO2/Na2O ratio = 1.6) as high viscosity exfoliating medium. The process led to BNNSs yield of nearly 30%. As the sheared suspension was neutralized with HCl, BNNSs with lateral size of approximately 250 nm and narrow size distribution, were found to align into perfectly parallel rows. High-resolution transmission electron microscopy (HR-TEM) analysis confirmed how WG preserved the integrity of the exfoliated BNNS in comparison with an analogous route with sole hydroxide, resulting in a high amount of BNNSs with undamaged structure. (C) 2021 Published by Elsevier B.V.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20504 - Ceramics

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2021

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

MATERIALS LETTERS

ISSN

0167-577X

e-ISSN

1873-4979

Svazek periodika

292

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

4

Strana od-do

„129551-1“-„129551-4“

Kód UT WoS článku

000639094100043

EID výsledku v databázi Scopus

2-s2.0-85101971294