The Corrosion Resistance of Hard Anodised EN AW 7075 T6 Alloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F21%3APU143189" target="_blank" >RIV/00216305:26620/21:PU143189 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/60162694:G43__/23:00558243

Výsledek na webu

<a href="https://iopscience.iop.org/article/10.1149/10501.0329ecst" target="_blank" >https://iopscience.iop.org/article/10.1149/10501.0329ecst</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1149/10501.0329ecst" target="_blank" >10.1149/10501.0329ecst</a>

Jazyk výsledku

angličtina

Název v původním jazyce

The Corrosion Resistance of Hard Anodised EN AW 7075 T6 Alloy

Popis výsledku v původním jazyce

In this paper, commercially cold-rolled and artificial aged EN AW 7075 T6 alloy has been used. To ensure increased corrosion resistance, surface hardness, scratching resistance, and aesthetic features, this aluminium alloy was subsequently hard anodised and hot-water sealed (AC-A). The hard anodizing and sealing process increased surface hardness up to 304 13 HV 1 from an initial surface hardness of 194 3 HV 1. Also, the microhardness of the anodised layer and bulk material has been documented. Scanning electron microscopy (SEM) was used for microstructure and trapped precipitates investigation in the 42.9 1.4 thick formed anodised layer investigation. The T6 treated (AC) and hard anodised together with sealed (AC-A) EN AW 7075 alloy corrosion properties were evaluated using the anodic potentiodynamic polarisation tests (PPT) in a neutral 2.5% NaCl deaerated solution. The corrosion rate CR (mm/y) decreased approx. 39-times for the hard anodised and sealed EN AW 7075 alloy (AC-A), associated with the shift of the E corr (mV) to more positive values, degreased Icorr (µA) and increased Rp (Ohm) values compared to the artificial aged (AC) alloy. Additionally, the pitting was evaluated using laser confocal microscopy, and the pitting coefficient was also calculated.

Název v anglickém jazyce

The Corrosion Resistance of Hard Anodised EN AW 7075 T6 Alloy

Popis výsledku anglicky

In this paper, commercially cold-rolled and artificial aged EN AW 7075 T6 alloy has been used. To ensure increased corrosion resistance, surface hardness, scratching resistance, and aesthetic features, this aluminium alloy was subsequently hard anodised and hot-water sealed (AC-A). The hard anodizing and sealing process increased surface hardness up to 304 13 HV 1 from an initial surface hardness of 194 3 HV 1. Also, the microhardness of the anodised layer and bulk material has been documented. Scanning electron microscopy (SEM) was used for microstructure and trapped precipitates investigation in the 42.9 1.4 thick formed anodised layer investigation. The T6 treated (AC) and hard anodised together with sealed (AC-A) EN AW 7075 alloy corrosion properties were evaluated using the anodic potentiodynamic polarisation tests (PPT) in a neutral 2.5% NaCl deaerated solution. The corrosion rate CR (mm/y) decreased approx. 39-times for the hard anodised and sealed EN AW 7075 alloy (AC-A), associated with the shift of the E corr (mV) to more positive values, degreased Icorr (µA) and increased Rp (Ohm) values compared to the artificial aged (AC) alloy. Additionally, the pitting was evaluated using laser confocal microscopy, and the pitting coefficient was also calculated.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20506 - Coating and films

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2021

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

ECS Transactions

ISBN

9781607685395

ISSN

1938-5862

e-ISSN

1938-6737

Počet stran výsledku

9

Strana od-do

329-337

Název nakladatele

Electrochemical Society

Místo vydání

neuveden

Místo konání akce

Brno

Datum konání akce

22. 8. 2021

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—