TiO2 nanotube layers decorated by titania nanoparticles as anodes for Li-ion microbatteries
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F22%3APU142163" target="_blank" >RIV/00216305:26620/22:PU142163 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/00216275:25310/22:39918051
Výsledek na webu
<a href="https://www.sciencedirect.com/science/article/pii/S0254058421011202" target="_blank" >https://www.sciencedirect.com/science/article/pii/S0254058421011202</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.matchemphys.2021.125337" target="_blank" >10.1016/j.matchemphys.2021.125337</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
TiO2 nanotube layers decorated by titania nanoparticles as anodes for Li-ion microbatteries
Popis výsledku v původním jazyce
In this work, the utilization of TiO2 nanotube (TNT) layers decorated with TiO2 nanoparticles (NPs) as anodes in Li-ion microbatteries is reported for the first time. Such TiO2 NPs decorated TNT layers possess an increased amount of active material and a higher surface area compared with their non-decorated (blank) counterparts. TNT layers decorated with several different amounts of TiO2 NPs were tested by galvanostatic cycling tests. The capacities of the TiO2 NPs decorated TNT layer anodes increase with the amount of NPs decoration due to the enhancement of the capacitive effect. Indeed, an areal capacity of -126 pAh cm(-2) (vs 88 pAh cm(-2) for the non decorated TNT layer) at the 200th cycle has been obtained after optimizing the NPs loading. On the other hand, a too high NPs loading of the TNT layers leads to a reduced areal capacity due to clogging of the nanotube exteriors and a significant decrease in inner diameter of the nanotubes.
Název v anglickém jazyce
TiO2 nanotube layers decorated by titania nanoparticles as anodes for Li-ion microbatteries
Popis výsledku anglicky
In this work, the utilization of TiO2 nanotube (TNT) layers decorated with TiO2 nanoparticles (NPs) as anodes in Li-ion microbatteries is reported for the first time. Such TiO2 NPs decorated TNT layers possess an increased amount of active material and a higher surface area compared with their non-decorated (blank) counterparts. TNT layers decorated with several different amounts of TiO2 NPs were tested by galvanostatic cycling tests. The capacities of the TiO2 NPs decorated TNT layer anodes increase with the amount of NPs decoration due to the enhancement of the capacitive effect. Indeed, an areal capacity of -126 pAh cm(-2) (vs 88 pAh cm(-2) for the non decorated TNT layer) at the 200th cycle has been obtained after optimizing the NPs loading. On the other hand, a too high NPs loading of the TNT layers leads to a reduced areal capacity due to clogging of the nanotube exteriors and a significant decrease in inner diameter of the nanotubes.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
10405 - Electrochemistry (dry cells, batteries, fuel cells, corrosion metals, electrolysis)
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2022
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
MATERIALS CHEMISTRY AND PHYSICS
ISSN
0254-0584
e-ISSN
1879-3312
Svazek periodika
276
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
7
Strana od-do
1-7
Kód UT WoS článku
000711213500002
EID výsledku v databázi Scopus
2-s2.0-85117227318