Liquid phase sintering of yttrium oxide: The effect of Al2O3 and SiO2 additives

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F24%3APU155517" target="_blank" >RIV/00216305:26620/24:PU155517 - isvavai.cz</a>

Výsledek na webu

<a href="https://www.sciencedirect.com/science/article/pii/S0955221923006817?via%3Dihub" target="_blank" >https://www.sciencedirect.com/science/article/pii/S0955221923006817?via%3Dihub</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.jeurceramsoc.2023.08.055" target="_blank" >10.1016/j.jeurceramsoc.2023.08.055</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Liquid phase sintering of yttrium oxide: The effect of Al2O3 and SiO2 additives

Popis výsledku v původním jazyce

Solid-state sintering of Y2O3 is difficult and requires high-temperature heat treatment or the use of a sintering additive. In this study, liquid-phase sintering was utilized to produce dense Y2O3 bodies with fine-grained microstructure. Al2O3 and SiO2 were added to a commercial nano-Y2O3 powder using aluminum nitrate and tetraethylorthosilicate (TEOS) as the precursors; the samples were uniaxially pressed at 100 MPa and sintered at 1500 degrees C and 1650 degrees C. The addition of the sintering aids increased the relative density of the samples sintered at lower temperatures; also, the sintering aids suppressed grain growth. The dissolution of Y2O3 into the liquid phase changes the solid-liquid interfacial energy resulting in the formation of isolated yttrium-silicate/yttriumaluminate grains and accounts for the suppression of the growth of yttria grains.

Název v anglickém jazyce

Liquid phase sintering of yttrium oxide: The effect of Al2O3 and SiO2 additives

Popis výsledku anglicky

Solid-state sintering of Y2O3 is difficult and requires high-temperature heat treatment or the use of a sintering additive. In this study, liquid-phase sintering was utilized to produce dense Y2O3 bodies with fine-grained microstructure. Al2O3 and SiO2 were added to a commercial nano-Y2O3 powder using aluminum nitrate and tetraethylorthosilicate (TEOS) as the precursors; the samples were uniaxially pressed at 100 MPa and sintered at 1500 degrees C and 1650 degrees C. The addition of the sintering aids increased the relative density of the samples sintered at lower temperatures; also, the sintering aids suppressed grain growth. The dissolution of Y2O3 into the liquid phase changes the solid-liquid interfacial energy resulting in the formation of isolated yttrium-silicate/yttriumaluminate grains and accounts for the suppression of the growth of yttria grains.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20504 - Ceramics

Projekt

<a href="/cs/project/GA20-14237S" target="_blank" >GA20-14237S: Zlepšení mikrostruktury a funkčních vlastností transparentních keramik pomocí distribuce dopantů - kombinovaný experimentální a teoretický přístup</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2024

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY

ISSN

0955-2219

e-ISSN

1873-619X

Svazek periodika

44

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

10

Strana od-do

383-392

Kód UT WoS článku

001089157700001

EID výsledku v databázi Scopus

2-s2.0-85169916891