Ultra-fine grained Aluminium Sheets Prepared by Accumulative Roll Bonding

Popis výsledku v původním jazyce

Accumulative Roll Bonding (ARB) produces bulk ultra-fine grained (UFG) sheets thus, it is suitable for industrial applications. ARB involves repetitions of surface processing, stacking, rolling bonding the sheets, and cutting. 6 to 8 cycles produce UFG materials with high strength and good ductility. Fine particles and small grain size are characteristic for continuously cast sheets so they are good starting materials for ARB. The ARB processing of pure Al at room temperature and of hot ARB of AlFeMn sheets is presented. In Al, hardness increases significantly only after the first 2 cycles. Positron lifetime measurements (PAS) revealed high dislocation density increase only after 1. cycle. PAS, OIM and TEM gave evidence for substantial grain refinement. In AlFeMn sheets with 2 cycles at 200°C, the grain size is of 400 to 800 nm and areas with grains of size 100-300 nm were found. ARB of AlFeMn sheet at 250, 300 and 350°C results in better bonding but in smaller increase in hardness.

Název v anglickém jazyce

Ultra-fine grained Aluminium Sheets Prepared by Accumulative Roll Bonding

Popis výsledku anglicky

Accumulative Roll Bonding (ARB) produces bulk ultra-fine grained (UFG) sheets thus, it is suitable for industrial applications. ARB involves repetitions of surface processing, stacking, rolling bonding the sheets, and cutting. 6 to 8 cycles produce UFG materials with high strength and good ductility. Fine particles and small grain size are characteristic for continuously cast sheets so they are good starting materials for ARB. The ARB processing of pure Al at room temperature and of hot ARB of AlFeMn sheets is presented. In Al, hardness increases significantly only after the first 2 cycles. Positron lifetime measurements (PAS) revealed high dislocation density increase only after 1. cycle. PAS, OIM and TEM gave evidence for substantial grain refinement. In AlFeMn sheets with 2 cycles at 200°C, the grain size is of 400 to 800 nm and areas with grains of size 100-300 nm were found. ARB of AlFeMn sheet at 250, 300 and 350°C results in better bonding but in smaller increase in hardness.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F03%2F0790" target="_blank" >GA106/03/0790: Superjemnozrnné hliníkové materiály připravené metodou intenzivní plastické deformace</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Nano 04

ISBN

80-214-2793-0

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

73-78

Název nakladatele

ČSNMT Praha

Místo vydání

Brno

Místo konání akce

Brno

Datum konání akce

13. 10. 2004

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—