Mikrostruktura a mechanické vlastnosti Al-Mg plechů vyrobených litím mezi válce

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25604716%3A_____%2F04%3A00010698" target="_blank" >RIV/25604716:_____/04:00010698 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68407700:21340/04:04099768

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Microstructure and mechanical properties of twin-roll cast Al-Mg sheets

Popis výsledku v původním jazyce

The influence of specific processing routes on the microstructure, texture, mechanical and technological properties of two commercial twin-roll cast alloys - AlMg2Mn0.8 (AA5049) and AlMg3 (AA5754) - was investigated. Sheets of 1.0 mm gauge were preparedin laboratory conditions with and without homogenization treatment. Non-homogenized samples were rolled also in industrial conditions. Surprisingly, it was found that homogenization results in grain coarsening and degradation of sheet anisotropy. Sheetsproduced by cold rolling from as-cast thickness of 6.0 mm directly to thickness of 1.0 mm and final annealing exhibit very fine grain size, higher strength combined with higher elongation and lower anisotropy as compared to the homogenized variant. The structure and mechanical properties of materials processed in laboratory and in industrial conditions are slightly different.

Název v anglickém jazyce

Microstructure and mechanical properties of twin-roll cast Al-Mg sheets

Popis výsledku anglicky

The influence of specific processing routes on the microstructure, texture, mechanical and technological properties of two commercial twin-roll cast alloys - AlMg2Mn0.8 (AA5049) and AlMg3 (AA5754) - was investigated. Sheets of 1.0 mm gauge were preparedin laboratory conditions with and without homogenization treatment. Non-homogenized samples were rolled also in industrial conditions. Surprisingly, it was found that homogenization results in grain coarsening and degradation of sheet anisotropy. Sheetsproduced by cold rolling from as-cast thickness of 6.0 mm directly to thickness of 1.0 mm and final annealing exhibit very fine grain size, higher strength combined with higher elongation and lower anisotropy as compared to the homogenized variant. The structure and mechanical properties of materials processed in laboratory and in industrial conditions are slightly different.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/OE126" target="_blank" >OE126: Technologie výroby hliníkových plechů pro použití v dopravě z plynule odlévaných materiálů</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2004

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Kovové materiály

ISSN

0023-432X

e-ISSN

—

Svazek periodika

42

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

SK - Slovenská republika

Počet stran výsledku

13

Strana od-do

193-205

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—