Účinky žíhání ve slitinách Al-Sc
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25604716%3A_____%2F07%3A%230000010" target="_blank" >RIV/25604716:_____/07:#0000010 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/00216208:11320/07:00004420
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Annealing Effects in Al-Sc Alloys
Popis výsledku v původním jazyce
Al-0.5Sc-0.4Zr and Al-2.7Mg0.14Sc-0.045Zr alloys were prepared by powder metallurgy (PM). Both materials contained a fine dispersion of spherical Al3(Sc1-xZrx) particles developed during extrusion at 350°C. Cold and hot rolling of as extruded Al-2.7Mg-0.14Sc-0.045Zr alloy influence the isochronal annealing curves of electrical resistivity. Measured relative resistivity changes reflect recovery of dislocation structure as well as precipitation and dissolution of beta'', beta' and/or beta phases of Al-Mgsystem and Al3(Sc1-xZrx) phase. Precipitation of very fine GP zones or particles of beta'' phase increases resistivity of both as extruded and cold rolled Al-2.7Mg-0.14Sc-0.045Zr alloy. Despite of recovery of dislocations in cold rolled Al-2.7Mg-0.14Sc-0.045Zr alloy between 150°C-180°C, isochronal annealing curves of hardness HV10 show, that very good mechanical properties persist up to 350°C due to the stability of Al3(Sc1-xZrx) phase particles.
Název v anglickém jazyce
Annealing Effects in Al-Sc Alloys
Popis výsledku anglicky
Al-0.5Sc-0.4Zr and Al-2.7Mg0.14Sc-0.045Zr alloys were prepared by powder metallurgy (PM). Both materials contained a fine dispersion of spherical Al3(Sc1-xZrx) particles developed during extrusion at 350°C. Cold and hot rolling of as extruded Al-2.7Mg-0.14Sc-0.045Zr alloy influence the isochronal annealing curves of electrical resistivity. Measured relative resistivity changes reflect recovery of dislocation structure as well as precipitation and dissolution of beta'', beta' and/or beta phases of Al-Mgsystem and Al3(Sc1-xZrx) phase. Precipitation of very fine GP zones or particles of beta'' phase increases resistivity of both as extruded and cold rolled Al-2.7Mg-0.14Sc-0.045Zr alloy. Despite of recovery of dislocations in cold rolled Al-2.7Mg-0.14Sc-0.045Zr alloy between 150°C-180°C, isochronal annealing curves of hardness HV10 show, that very good mechanical properties persist up to 350°C due to the stability of Al3(Sc1-xZrx) phase particles.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA106%2F04%2F1353" target="_blank" >GA106/04/1353: Vliv podmínek rozpadu tuhého roztoku na strukturu a vlastnosti systému Al-Mg-Sc-Zr</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2007
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Materials Science and Engineering A
ISSN
0921-5093
e-ISSN
—
Svazek periodika
462
Číslo periodika v rámci svazku
1-2
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
5
Strana od-do
370-374
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—