The Participation of Macrocell Activity on Corrosion of steel in Concrete
Popis výsledku v původním jazyce
Makrocell activity is characterized by a dependence of the corrosion intensity at the anode on the surface area ratio of the anode and the cathode. In cases where road structures build of reinforced concrete are contaminated by chlorides the ratio of cathode surface to the anode area. The kinetics of oxygen reduction may depend not only on the rate of transport of oxygen but also on the catalytic properties of the metallic surface on which the reaction is taking place. It is generally known that redox reactions on passive metals including iron proceed at low exchange currents. The rate of oxygen reduction was measured as a function of potential of the metal electrodes under study using both potentiostatic and potentiodynamic techniques. The potentiostatic measurement were run in potential step of - 100 mV, with a hold for 120s at each constant potential, in an aerated and slightly agitated cement suspension containing 20 g cement in 400 ml water, at laboratory temperature. The current
Název v anglickém jazyce
The Participation of Macrocell Activity on Corrosion of steel in Concrete
Popis výsledku anglicky
Makrocell activity is characterized by a dependence of the corrosion intensity at the anode on the surface area ratio of the anode and the cathode. In cases where road structures build of reinforced concrete are contaminated by chlorides the ratio of cathode surface to the anode area. The kinetics of oxygen reduction may depend not only on the rate of transport of oxygen but also on the catalytic properties of the metallic surface on which the reaction is taking place. It is generally known that redox reactions on passive metals including iron proceed at low exchange currents. The rate of oxygen reduction was measured as a function of potential of the metal electrodes under study using both potentiostatic and potentiodynamic techniques. The potentiostatic measurement were run in potential step of - 100 mV, with a hold for 120s at each constant potential, in an aerated and slightly agitated cement suspension containing 20 g cement in 400 ml water, at laboratory temperature. The current
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JK - Koroze a povrchové úpravy materiálu
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA106%2F02%2F1019" target="_blank" >GA106/02/1019: Studium počátečního stadia porušování pasivity povrchu ocelových výztuží v betonu vlivem chloridových iontů</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2004
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
EUROCORR 2005
ISBN
—
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
11-16
Název nakladatele
EUROCORR
Místo vydání
Lisboa
Místo konání akce
Lisboa
Datum konání akce
1. 1. 2005
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—