Chemical composition of new copper alloys for machining and its effect on their susceptibility to corrosion cracking

Popis výsledku v původním jazyce

Zinc-containing copper alloys, the so-called alpha + beta brasses, are commonly used in contact with potable water. These materials are alloyed with lead to improve machinability. In wrought special brass alloys, reducing the content of this alloying element or replacing it with alternative alloying additions may give rise to a new type of machinable copper alloys which differ from the original alloys by their contents of other modifier elements such as Si {or possibly, Mg. Bi, and I1). These alloys have a very low content of lead required for the break-up of chips during machining. Even though these types of brass exhibit a very good machinability, the effects of their chemical composition on the resistance of the alloy lo corrosion cracking have notyet been given sufficient attention.

Název v anglickém jazyce

Chemical composition of new copper alloys for machining and its effect on their susceptibility to corrosion cracking

Popis výsledku anglicky

Zinc-containing copper alloys, the so-called alpha + beta brasses, are commonly used in contact with potable water. These materials are alloyed with lead to improve machinability. In wrought special brass alloys, reducing the content of this alloying element or replacing it with alternative alloying additions may give rise to a new type of machinable copper alloys which differ from the original alloys by their contents of other modifier elements such as Si {or possibly, Mg. Bi, and I1). These alloys have a very low content of lead required for the break-up of chips during machining. Even though these types of brass exhibit a very good machinability, the effects of their chemical composition on the resistance of the alloy lo corrosion cracking have notyet been given sufficient attention.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JK - Koroze a povrchové úpravy materiálu

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F04%2F0122" target="_blank" >GA106/04/0122: Studium vlastností modelových slitin mědi se sníženým obsahem nízkotavitelných kovů určených pro obrábění</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials and Corrosion / Werkstoffe und Korrosion

ISSN

0947-5117

e-ISSN

—

Svazek periodika

58

Číslo periodika v rámci svazku

9

Stát vydavatele periodika

DE - Spolková republika Německo

Počet stran výsledku

6

Strana od-do

661-666

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—