STUDY OF DEGRADATION MECHANISMS OF ZINCSILICATE COATING

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25794787%3A_____%2F09%3A%230000410" target="_blank" >RIV/25794787:_____/09:#0000410 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
STUDY OF DEGRADATION MECHANISMS OF ZINCSILICATE COATING
Popis výsledku v původním jazyce
Tested paint systems had been zinc silicate primer with high concentration of metallic zinc pigment and two-components inorganic top coat. Coating was applied on steel samples with different surface treatment. Samples had been exposed in accelerated corrosion tests and at atmospheric test site. The intensity of degradation is different according to exposure conditions and surface treatment of the samples.
Název v anglickém jazyce
STUDY OF DEGRADATION MECHANISMS OF ZINCSILICATE COATING
Popis výsledku anglicky
Tested paint systems had been zinc silicate primer with high concentration of metallic zinc pigment and two-components inorganic top coat. Coating was applied on steel samples with different surface treatment. Samples had been exposed in accelerated corrosion tests and at atmospheric test site. The intensity of degradation is different according to exposure conditions and surface treatment of the samples.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JK - Koroze a povrchové úpravy materiálu
OECD FORD obor
—

Projekt
<a href="/cs/project/GA104%2F07%2F1637" target="_blank" >GA104/07/1637: Studium faktorů ovlivňujících vlastnosti a mechanismus degradace organických povlaků</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění
2009
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)