A self-destroying mechanism generated when functional parameters of paint system layers are improved in a non-suitable manner

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25794787%3A_____%2F17%3AN0000003" target="_blank" >RIV/25794787:_____/17:N0000003 - isvavai.cz</a>

Výsledek na webu

<a href="https://www.degruyter.com/downloadpdf/j/kom.2017.61.issue-1/kom-2017-0004/kom-2017-0004.pdf" target="_blank" >https://www.degruyter.com/downloadpdf/j/kom.2017.61.issue-1/kom-2017-0004/kom-2017-0004.pdf</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1515/kom-2017-0004" target="_blank" >10.1515/kom-2017-0004</a>

Jazyk výsledku

angličtina

Název v původním jazyce

A self-destroying mechanism generated when functional parameters of paint system layers are improved in a non-suitable manner

Popis výsledku v původním jazyce

Increasing the functional parameters of coating composition-based protective coatings is a strongly emerging trend. However, there are some limits to the increasing of utility parameters of protective coatings – always where such parameters are opposite to the basic property, which is corrosion protection. The presented study describes a case of a premature failure in the corrosion protection secured by a duplex system that occurred after the paint system had been enriched with an anti-sliding property.

Název v anglickém jazyce

A self-destroying mechanism generated when functional parameters of paint system layers are improved in a non-suitable manner

Popis výsledku anglicky

Increasing the functional parameters of coating composition-based protective coatings is a strongly emerging trend. However, there are some limits to the increasing of utility parameters of protective coatings – always where such parameters are opposite to the basic property, which is corrosion protection. The presented study describes a case of a premature failure in the corrosion protection secured by a duplex system that occurred after the paint system had been enriched with an anti-sliding property.

Druh

J_SC - Článek v periodiku v databázi SCOPUS

CEP obor

—

OECD FORD obor

20506 - Coating and films

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2017

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Koroze a ochrana materiálu

ISSN

1804-1213

e-ISSN

—

Svazek periodika

61

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

7

Strana od-do

32-38

Kód UT WoS článku

—

EID výsledku v databázi Scopus

2-s2.0-85014605366