Crack growth anomalies in HAZ for parent steel P91
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25797000%3A_____%2F03%3A00007285" target="_blank" >RIV/25797000:_____/03:00007285 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/00216208:11320/04:00002516 RIV/25797000:_____/04:#0000005
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Crack growth anomalies in HAZ for parent steel P91
Popis výsledku v původním jazyce
The rate of creep crack growth in the intercritical layer of HAZ for parent steel P91 is measured for a range of loads at 600 deg C. The TDCB samples were used, the test times ranging from 19 to 6603 h. The crack tip parameter C*(t) was calculated usingline displacements due to creep, the latter obtained from permanent deflections as corrected on instant plasticity.For long term tests, relatively high growth rates appear so that no unique asymptotic power law exists for all load regimes. Furthermore, an anomalous range of load dependence on crack initiation times was revealed. An attempt is made to correlate these effects with changes in ductility due to possible re-precipitation during thermomechanical exposition.
Název v anglickém jazyce
Crack growth anomalies in HAZ for parent steel P91
Popis výsledku anglicky
The rate of creep crack growth in the intercritical layer of HAZ for parent steel P91 is measured for a range of loads at 600 deg C. The TDCB samples were used, the test times ranging from 19 to 6603 h. The crack tip parameter C*(t) was calculated usingline displacements due to creep, the latter obtained from permanent deflections as corrected on instant plasticity.For long term tests, relatively high growth rates appear so that no unique asymptotic power law exists for all load regimes. Furthermore, an anomalous range of load dependence on crack initiation times was revealed. An attempt is made to correlate these effects with changes in ductility due to possible re-precipitation during thermomechanical exposition.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2004
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Kovové materiály
ISSN
0023-432X
e-ISSN
—
Svazek periodika
neuveden
Číslo periodika v rámci svazku
v tisku
Stát vydavatele periodika
SK - Slovenská republika
Počet stran výsledku
14
Strana od-do
1-14
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—