Influence of Microstructure on Hydrogen Induced Cracking in Gas Pipeline Steels

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25797000%3A_____%2F10%3A%230000216" target="_blank" >RIV/25797000:_____/10:#0000216 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Influence of Microstructure on Hydrogen Induced Cracking in Gas Pipeline Steels
Popis výsledku v původním jazyce
In this article are described results of evaluation and measurement of hydrogen induced cracks and blisters in gas pipeline steels. Quantitative values characterizing hydrogen induced cracking were given into correlation with microstructure. Main reasonfor susceptibility of these steels to hydrogen induced cracking was found in pearlite banding.
Název v anglickém jazyce
Influence of Microstructure on Hydrogen Induced Cracking in Gas Pipeline Steels
Popis výsledku anglicky
In this article are described results of evaluation and measurement of hydrogen induced cracks and blisters in gas pipeline steels. Quantitative values characterizing hydrogen induced cracking were given into correlation with microstructure. Main reasonfor susceptibility of these steels to hydrogen induced cracking was found in pearlite banding.

Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku
METAL 2010: 19th International Metallurgical and Materials Conference
ISBN
978-80-87294-17-8
ISSN
—
e-ISSN
—
Počet stran výsledku
5
Strana od-do
—
Název nakladatele
TANGER, spol s r.o.
Místo vydání
Ostrava, Česká Republika
Místo konání akce
Rožnov pod Radhoštěm, ČR
Datum konání akce
1. 1. 2010
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—

Podobné výsledky(10)