Effect of Inclusions on Fatigue Strength of Heat Treated Components
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25797000%3A_____%2F10%3A%230000225" target="_blank" >RIV/25797000:_____/10:#0000225 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Effect of Inclusions on Fatigue Strength of Heat Treated Components
Popis výsledku v původním jazyce
Inclusions significantly affect fatigue properties of quenched and tempered parts. Data about inclusions importance during an initiation of fatigue fractures were acquired within the frame of systematical fatigue tests carried out for fatigue propertiesverification of CrNiMo (V) steels quenched and tempered to 800 - 1000 MPa strenght. A valuable set of fatigue fractures from the high lifetime area was acquired. Carried out microfractographic analysis of these fractures allowed critically evaluate the influence of inclusions, their dimensions, character and morphology on the initiation and propagation of the fatigue fractures in the area of fatigue strenght. Comparison of inclusions size ?a? after Murakami with size determined experimentally. Limitinginfluence of small single inclusions in the structure. Initiation of secondary fatigue cracks on inclusions outside of the fracture initiation area. Danger of the fracture initiation after very high lifetime.
Název v anglickém jazyce
Effect of Inclusions on Fatigue Strength of Heat Treated Components
Popis výsledku anglicky
Inclusions significantly affect fatigue properties of quenched and tempered parts. Data about inclusions importance during an initiation of fatigue fractures were acquired within the frame of systematical fatigue tests carried out for fatigue propertiesverification of CrNiMo (V) steels quenched and tempered to 800 - 1000 MPa strenght. A valuable set of fatigue fractures from the high lifetime area was acquired. Carried out microfractographic analysis of these fractures allowed critically evaluate the influence of inclusions, their dimensions, character and morphology on the initiation and propagation of the fatigue fractures in the area of fatigue strenght. Comparison of inclusions size ?a? after Murakami with size determined experimentally. Limitinginfluence of small single inclusions in the structure. Initiation of secondary fatigue cracks on inclusions outside of the fracture initiation area. Danger of the fracture initiation after very high lifetime.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2010
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
COMMUNICATIONS
ISSN
1335-4205
e-ISSN
—
Svazek periodika
Volume 12
Číslo periodika v rámci svazku
4
Stát vydavatele periodika
SK - Slovenská republika
Počet stran výsledku
7
Strana od-do
—
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—