Fatigue Resistance and Crack Initiation Mechanisms in Nitrided Steel Treated with Selected Types of Surface Coating
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25797000%3A_____%2F13%3A%230000297" target="_blank" >RIV/25797000:_____/13:#0000297 - isvavai.cz</a>
Výsledek na webu
<a href="http://www.scientific.net/MSF" target="_blank" >http://www.scientific.net/MSF</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientific.net/MSF.730-732.203" target="_blank" >10.4028/www.scientific.net/MSF.730-732.203</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Fatigue Resistance and Crack Initiation Mechanisms in Nitrided Steel Treated with Selected Types of Surface Coating
Popis výsledku v původním jazyce
In the paper, results of an experimental programme aimed at evaluation of fatigue resistance at repeated loading of nitrided steel after application of two types of coating, (i) nanostructured C-layer deposited by a modified cathodic arc technique according to Microcoat patent and (ii) Cr-WC:H-DLC layer produced according to Hauzer patent, are presented and discussed. Results and analyses showed that coating effects depended on the specific technology and parameters. The Cr-WC:H-DLC layer affected fatigue limit favourably unlike the Microcoat C-layer, which resulted in reduction of fatigue strength.
Název v anglickém jazyce
Fatigue Resistance and Crack Initiation Mechanisms in Nitrided Steel Treated with Selected Types of Surface Coating
Popis výsledku anglicky
In the paper, results of an experimental programme aimed at evaluation of fatigue resistance at repeated loading of nitrided steel after application of two types of coating, (i) nanostructured C-layer deposited by a modified cathodic arc technique according to Microcoat patent and (ii) Cr-WC:H-DLC layer produced according to Hauzer patent, are presented and discussed. Results and analyses showed that coating effects depended on the specific technology and parameters. The Cr-WC:H-DLC layer affected fatigue limit favourably unlike the Microcoat C-layer, which resulted in reduction of fatigue strength.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2013
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Materials Science Forum
ISSN
1662-9752
e-ISSN
—
Svazek periodika
730-732
Číslo periodika v rámci svazku
První čtvrtletí
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
6
Strana od-do
203-208
Kód UT WoS článku
000315545200034
EID výsledku v databázi Scopus
—