An effect of surface laser hardening on deformations and fatigue properties of 42CrMo4 steel specimens

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25797000%3A_____%2F14%3A%230000474" target="_blank" >RIV/25797000:_____/14:#0000474 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.scientific.net/AMM" target="_blank" >http://www.scientific.net/AMM</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.4028/www.scientific.net/AMM.486.54" target="_blank" >10.4028/www.scientific.net/AMM.486.54</a>

Jazyk výsledku

angličtina

Název v původním jazyce

An effect of surface laser hardening on deformations and fatigue properties of 42CrMo4 steel specimens

Popis výsledku v původním jazyce

Results of an experimental investigation of effects of laser treatment with selected parameters on deformations and fatigue resistance of relatively small samples of 8 x 8 mm cross section are presented and discussed in this work. Effects of surface speed of the laser beam was evaluated, then effects of fixation of the specimens to rigid supporting steel plate on changes of deflection caused by the laser treatment and eventually, changes of the deformations after releasing the specimens from the supporting plate. Results are in a good agreement with residual stress measurements. Fatigue tests indicated possibilities of favourable effects of laser treatment on fatigue resistance. Results are discussed considering an occurrence of inclusions in the material, residual stresses and fatigue damage mechanisms.

Název v anglickém jazyce

An effect of surface laser hardening on deformations and fatigue properties of 42CrMo4 steel specimens

Popis výsledku anglicky

Results of an experimental investigation of effects of laser treatment with selected parameters on deformations and fatigue resistance of relatively small samples of 8 x 8 mm cross section are presented and discussed in this work. Effects of surface speed of the laser beam was evaluated, then effects of fixation of the specimens to rigid supporting steel plate on changes of deflection caused by the laser treatment and eventually, changes of the deformations after releasing the specimens from the supporting plate. Results are in a good agreement with residual stress measurements. Fatigue tests indicated possibilities of favourable effects of laser treatment on fatigue resistance. Results are discussed considering an occurrence of inclusions in the material, residual stresses and fatigue damage mechanisms.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JL - Únava materiálu a lomová mechanika

OECD FORD obor

—

Projekt

<a href="/cs/project/FR-TI3%2F814" target="_blank" >FR-TI3/814: Optimalizace laserového povrchového zpracování strojních součástí pro zvýšení jejich užitných vlastností</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Applied Mechanics and Materials

ISSN

1660-9336

e-ISSN

—

Svazek periodika

486

Číslo periodika v rámci svazku

2014

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

4

Strana od-do

54-57

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—