MICROSTRUCTURE CHANGES OF P92 WELD DURING CREEP EXPOSURE

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25861697%3A_____%2F14%3A%230000025" target="_blank" >RIV/25861697:_____/14:#0000025 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

MICROSTRUCTURE CHANGES OF P92 WELD DURING CREEP EXPOSURE

Popis výsledku v původním jazyce

This work is a contribution to the research of modified heat resistant steel P92. This steel is currently one of the best modified chromium steels in terms of achieved values of creep rupture strength. The article is focused on microstructure investigation of P92 weld after creep deformation. Up to date results of creep rupture test of P92 welds are presented here too. The microstructure in the as welded condition and after long-term creep exposure (26.000 hours/600°C) of P92 welds has been investigatedand microstructural parameters were detrmined. Results of intercritical zone of heat affected zone (HAZ) are compared with parameters of parent material, which is not influence by welding. Results of TEM analyses reveal deteriorating effect of welding procedure on microstructure of P92 welds during subsequent creep exposure

Název v anglickém jazyce

MICROSTRUCTURE CHANGES OF P92 WELD DURING CREEP EXPOSURE

Popis výsledku anglicky

This work is a contribution to the research of modified heat resistant steel P92. This steel is currently one of the best modified chromium steels in terms of achieved values of creep rupture strength. The article is focused on microstructure investigation of P92 weld after creep deformation. Up to date results of creep rupture test of P92 welds are presented here too. The microstructure in the as welded condition and after long-term creep exposure (26.000 hours/600°C) of P92 welds has been investigatedand microstructural parameters were detrmined. Results of intercritical zone of heat affected zone (HAZ) are compared with parameters of parent material, which is not influence by welding. Results of TEM analyses reveal deteriorating effect of welding procedure on microstructure of P92 welds during subsequent creep exposure

Druh

D - Stať ve sborníku

CEP obor

JR - Ostatní strojírenství

OECD FORD obor

—

Projekt

<a href="/cs/project/FR-TI3%2F206" target="_blank" >FR-TI3/206: *Optimalizace technologií svařování a tepelného zpracování modifikované 9%Cr žáropevné oceli pro USC bloky tepelných elektráren.</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Metal 2014, Conference proceedings

ISBN

978-80-87294-54-3

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

464-469

Název nakladatele

TANGER Ltd.

Místo vydání

Ostrava

Místo konání akce

Hotel Voroněž, Brno

Datum konání akce

21. 5. 2014

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—