Studium mikrostruktury přechodového svaru kotlových trubek po dlouhodobé creepové expozici při 550°C
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25870807%3A_____%2F04%3A%230000011" target="_blank" >RIV/25870807:_____/04:#0000011 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Microstructural investigations on a dissimilar weld of boiler tubes after long - teerm creep exposure at 550°C
Popis výsledku v původním jazyce
The paper deals with microstructural characterization of a dissimilar weld joint made between a low alloy 12CrMoV6-2 steel and an AISI 316H steel using a 20Cr38Ni6Mo filler. The studies were carried out on a cross weld creep rupture specimen which failedafter exposure for 104 875 hours at 550°C. Fracture occurred in the intercritical region of the HAZ on the side of the low alloy steel. Optical microscopy, transmission electron microscopy and X-ray microanalysis were used for microstructural investigations on the low alloy steel HAZ and the adjacent carburized zone of the nickel bearing weld metal. The results proved the positive effect of vanadium in low alloy steels on microstructural evolution in critical regions of dissimilar welds.
Název v anglickém jazyce
Microstructural investigations on a dissimilar weld of boiler tubes after long - teerm creep exposure at 550°C
Popis výsledku anglicky
The paper deals with microstructural characterization of a dissimilar weld joint made between a low alloy 12CrMoV6-2 steel and an AISI 316H steel using a 20Cr38Ni6Mo filler. The studies were carried out on a cross weld creep rupture specimen which failedafter exposure for 104 875 hours at 550°C. Fracture occurred in the intercritical region of the HAZ on the side of the low alloy steel. Optical microscopy, transmission electron microscopy and X-ray microanalysis were used for microstructural investigations on the low alloy steel HAZ and the adjacent carburized zone of the nickel bearing weld metal. The results proved the positive effect of vanadium in low alloy steels on microstructural evolution in critical regions of dissimilar welds.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
Z - Vyzkumny zamer (s odkazem do CEZ)
Ostatní
Rok uplatnění
2004
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Acta Metallurgica Slovaca
ISSN
—
e-ISSN
—
Svazek periodika
1
Číslo periodika v rámci svazku
10
Stát vydavatele periodika
SK - Slovenská republika
Počet stran výsledku
4
Strana od-do
—
Kód UT WoS článku
—
EID výsledku v databázi Scopus
—