The effect of heat treatment on microstructure and properties of a 13Cr6Ni2.5Mo supermartensitic steel

Popis výsledku v původním jazyce

The paper deals with studies how tempering/intercritical annealing in temperature interval from 540 to 700°C affects mechanical properties and microstructure of a low carbon 13Cr6Ni2.5Mo supermartensitic steel. It has been proved that during tempering attemperatures above 590°C partial austenitization is accompanied by intensive precipitation of Fe2Mo Laves phase in the martensitic matrix. Thermocalc calculations confirmed that Fe2Mo Laves phase is the thermodynamically stable phase in the steel investigated. Precipitation of Laves phase is probably responsible for the fact that positive effect of reversed austenite fraction on impact toughness was not observed. The fraction of reverted austenite in the microstructure increased up to the tempering temperature of 600°C

Název v anglickém jazyce

The effect of heat treatment on microstructure and properties of a 13Cr6Ni2.5Mo supermartensitic steel

Popis výsledku anglicky

The paper deals with studies how tempering/intercritical annealing in temperature interval from 540 to 700°C affects mechanical properties and microstructure of a low carbon 13Cr6Ni2.5Mo supermartensitic steel. It has been proved that during tempering attemperatures above 590°C partial austenitization is accompanied by intensive precipitation of Fe2Mo Laves phase in the martensitic matrix. Thermocalc calculations confirmed that Fe2Mo Laves phase is the thermodynamically stable phase in the steel investigated. Precipitation of Laves phase is probably responsible for the fact that positive effect of reversed austenite fraction on impact toughness was not observed. The fraction of reverted austenite in the microstructure increased up to the tempering temperature of 600°C

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/FF-P2%2F053" target="_blank" >FF-P2/053: Výzkum a vývoj ocelí s vysokými užitnými vlastnostmi.</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2005

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Sborník vědeckých prací Vysoké školy báňské - Technické univerzity Ostrava

ISBN

80-248-0860-9

ISSN

—

e-ISSN

—

Počet stran výsledku

7

Strana od-do

225-231

Název nakladatele

Vysoká škola báňská - Technická univerzita Ostrava

Místo vydání

Ostrava-Poruba

Místo konání akce

Rožnov pod Radhoštěm

Datum konání akce

1. 1. 2005

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—