Mikrostrukturní parametry a vlastnosti oceli 15NiCuMoNb5 používané pro speciální aplikace

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25870807%3A_____%2F07%3A%230000074" target="_blank" >RIV/25870807:_____/07:#0000074 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Microstructural parameters and properties of 15NiCuMoNb5 grade steel used for special applications

Popis výsledku v původním jazyce

This article is focused on optimization of fundamental utility properties and technological process of advanced low alloy steel 15NiCuMoNb5 used for power engineering mainly for production of large capacity steam boilers. Consequently problem critical locality in weld after post weld heat treatment is studied. Optimization of welding technology is proposed. Fracture behaviour of welded joint made from boiler plates 80 mm in thickness of 15NiCuMoNb5 type steel after N + T PWHT regime after welding procedure were studied. Stable crack growth measurement and evaluation of fracture toughness of base material as well as weld metal in temperature region from 0 up 350°C were carried out. Unstable cleavage fracture and fracture toughness KJc of both parts of welded joint at test temperatures cover the transition region were evaluated. The reference temperature T0 approach was used for evaluation of temperature dependence of fracture toughness in transition range.

Název v anglickém jazyce

Microstructural parameters and properties of 15NiCuMoNb5 grade steel used for special applications

Popis výsledku anglicky

This article is focused on optimization of fundamental utility properties and technological process of advanced low alloy steel 15NiCuMoNb5 used for power engineering mainly for production of large capacity steam boilers. Consequently problem critical locality in weld after post weld heat treatment is studied. Optimization of welding technology is proposed. Fracture behaviour of welded joint made from boiler plates 80 mm in thickness of 15NiCuMoNb5 type steel after N + T PWHT regime after welding procedure were studied. Stable crack growth measurement and evaluation of fracture toughness of base material as well as weld metal in temperature region from 0 up 350°C were carried out. Unstable cleavage fracture and fracture toughness KJc of both parts of welded joint at test temperatures cover the transition region were evaluated. The reference temperature T0 approach was used for evaluation of temperature dependence of fracture toughness in transition range.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GP106%2F05%2FP541" target="_blank" >GP106/05/P541: Výzkum vztahů mezi mikrostrukturními parametry a vlastnostmi progresivních materiálů pro náročné průmyslové aplikace</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Manufacturing Technology

ISSN

1213-2489

e-ISSN

—

Svazek periodika

VII.

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

6

Strana od-do

37-42

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—